Corrosion behavior of lanthanum-based conversion coating modified with citric acid on hot dip galvanized steel in aerated 1M NaCl solution
Gang Kong,Liu Lingyan,Jintang Lu,Chunshan Che,Zheng Zhong
DOI: https://doi.org/10.1016/j.corsci.2011.01.038
IF: 7.72
2011-01-01
Corrosion Science
Abstract:Research highlights ► The corrosion behavior of lanthanum conversion coating modified with citric acid on hot dip galvanized (HDG) steel was investigated in aerated 1 M NaCl solution. ► The La salt conversion coatings inhibit both the anodic and cathodic responses of the system and hence prevent the HDG substrate from corrosion. ► The corrosion process of the coating can be divided into three stages. The outer layer of the coating was destroyed at the initial stage of immersion (<18 h), then the inner layer was damaged at the second stage (18–144 h), and the corrosion of the substrate played a dominant role at the finial stage (>144 h). Abstract Rare earth conversion coating is one of the most promising substitutes to the toxic chromate coating. The corrosion resistance of lanthanum conversion coating modified with citric acid on hot dip galvanized (HDG) steel was investigated in aerated 1 M NaCl solution by means of electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization measurements. Equivalent circuits were subsequently developed from the measurements to elucidate the corrosion behavior of the coating. The surface morphology of the lanthanum conversion coating was observed by scanning electron microscopy (SEM), and the chemical composition of the coating was characterized by energy dispersive spectroscopy (EDS). The results showed that the corrosion process of the modified lanthanum conversion coating consisted of three stages. The overall corrosion resistance of the coating was excellent. Keywords A. Rare earth elements B. EIS B. Polarization B. Erosion C. Passive films 1 Introduction Chromate passivation has been used extensively in surface treatment of metals until recent decades when the toxicity of Cr(VI) came under scrutiny in increasing number of countries. It is now generally accepted that the chromate solution, although an excellent corrosion inhibitor, will eventually be phased out from manufacturing processes [1] . The research on the chromate replacements for zinc and zinc coating started in the late 1980s [2–10] . Molybdate, silane, silicate, rare earth (RE) and phosphate salts have been studied extensively as alternative to toxic chromate for the corrosion protection of zinc and zinc coating. In the past decade, most research activities focused on single cerium conversion coating [11–16] and Ce compound coatings obtained using single or multiple step processes [17–21] . Those works reported the use of cerium salts for corrosion inhibition on different metals and alloys and proposed a cathodic mechanism to explain the formation of the RE oxide film. Recently, more attentions were paid to the modification of RE conversion coating with organic and inorganic inhibitors due to the simplicity and low cost of such modifications. One of the successful inhibitors used for the modification was citric acid, which is renewable and non-toxic. Tizpar and Ghasemi [22] reported that citric acid acted as a good corrosion inhibitor for the lead alloy exposed to sulfuric acid. Tselesh [23] employed potentiodynamic technique in his study on the anodic behavior of tin in citrate buffer solution and revealed that the passive layer formed on the anode surface effectively inhibited the further corrosion of tin. There were, however, few studies on the application of citric acid on the corrosion protection of galvanized steels. Extending a prior project on the subject [24] , the present study aims to characterize an environmentally acceptable La conversion coating modified by citric acid on Hot dip galvanized (HDG) steel. The corrosion behavior of the coating in aerated 1 M NaCl solution was investigated by means of electrochemical impedance spectroscopy (EIS) and by the polarization measurements. Equivalent circuit was also developed to study the corrosion process of the conversion coating. 2 Experimental Cold-rolled mild carbon steel coupons in the size of 40 mm × 30 mm × 2 mm were successively degreased, pickled, fluxed and dried before they were dipped in a molten zinc bath at 450 °C for 1 min. Coupons were withdrawn from the zinc bath at a controlled slow speed and were then immediately quenched in water. The galvanized steel coupons thus obtained were used as the substrate of the samples. The thickness of the galvanized coating measured by STH-1 thickness gauge was about 50 μm. Consistent with a procedure developed in a prior study [12] , the passivation solution was prepared by mixing analytical reagent grade of 20 g/L La(NO 3 ) 3 ·6H 2 O, 10 mL/L 30% ( v/v ) H 2 O 2 and 10 g/L citric acid (H 3 Cit) in aqueous solutions. The HDG samples were immersed into the passivation solution for 30 min at 70 °C and then dried in air. A modified La-based conversion coating was thereby obtained on the surface of the hot dip galvanized samples. The electrochemical experiments were performed by using a CHI640B electrochemical measurement workstation. The electrochemical cell consisted of a working electrode with an exposure area of 1 cm 2 , a saturated calomel electrode (SCE) as the reference electrode, and a platinum foil with an exposure area of 10 cm 2 as the counter electrode. Measurements were taken after the sample was immersed in an aerated 1 M NaCl solution at ambient temperature for 20 min and the corrosion potential had been stabilized. The perturbation and scan rate for potentiodynamic linear polarization (LPR) was ±10 mV and 1 mV/s, respectively. The electrochemical parameters such as the corrosion potential E corr , The corrosion currents i corr and the polarization resistance R p were obtained by fitting the Tafel slope of the polarization branches using the software package of CHI640B workstation. The measuring frequency for electrochemical impendence spectra (EIS) ranged from 10 5 down to 10 −2 Hz. The acquired measurement data were analyzed using the software package of CHI640B. The equivalent circuits of the EIS data were obtained from Zview. The surface morphology of the coatings was examined by scanning electron microscopy (SEM, PHILIPS; Model: XL-30-FEG). The chemical composition was analyzed by energy dispersive spectroscopy (EDS, OXFORD, Model: Inca300). 3 Results and discussion 3.1 Electrochemical behavior The electrochemical behavior of the HDG samples with or without La conversion coating in an aerated 1 M NaCl solution was evaluated by potentiodynamic polarization and the results are shown in Fig. 1 . Compared to the untreated HDG sample, the presence of a La coating on the HDG sample led to significant changes in both anodic and cathodic responses. The fitting results obtained from potentiodynamic polarization curves in Fig. 1 were listed in Table 1 . As seen from Table 1 , the corrosion potential E corr , as measured from Fig. 1 , was −1.062 V(SCE) for the untreated HDG sample and −1.116 V(SCE) for the sample with a La conversion coating. The decrease of E corr may be attributed to the effects of the La coating on the cathodic reaction. The corrosion currents i corr decreased by over one order of magnitude from 13.21 to 0.33 μA/cm 2 after the treatment. The decreases in the current densities were attributable to the coverage of the active area on the electrodes by the La coating. Correspondent to the decrease in corrosion current, the polarization resistance R p increased significantly from 0.49 to 26.84 kΩ cm 2 . The electrochemical impedance was measured under stable open circuit potential which was obtained after immersing the untreated and treated samples in 1 M NaCl solution for 20 min. The results are shown in Fig. 2 . The impedance was about 600 Ω cm 2 for the untreated samples and about 24 kΩ cm 2 for the La treated sample. The increase in impedance is consistent with the increase in polarization resistance discussed earlier. Compared to single RE salt conversion coating investigated in a prior study [20] , the modified La conversion coating possessed superior anti-corrosion properties. 3.2 Surface morphology of the La coating The micro appearance of the La conversion coating is shown in Fig. 3 . The surface morphology displayed certain degree of non-uniformity. In addition, a large number of cracks existed in the coating, forming a network that is reminiscent to a drought riverbed ( Fig. 3 a). Flaking of the coating can also be observed. It can be seen under higher magnifications ( Fig. 3 b) that some floccules were attached to the coating surface. 3.3 Corrosion process In order to investigate the corrosion process of the conversion coating, EIS measurements were carried out on the La coating samples at open circuit potential in 1 M NaCl solution for various times. Results shown in Fig. 4 reveal that the impedance values decreased with the immersion time in the NaCl solution. For the immersion time up to 18 h, three capacitive time constants can be easily distinguished in the Bode plots ( Fig. 4 a and b): one in the high frequency zone, another in the high to medium frequency range and the third in the low frequency zone. When the immersion time increased to over 18 h, diffusion impedance appeared. The two time constants in the higher frequency zones suggest that the conversion coating might consist of two layers, whereas the third time constant in the low frequency zone may be attributable to the charge transfer reactions taken place on the substrate. Three relaxation stages of the La conversion coating can be seen in the impedance plots from Fig. 4 . After 18 h of immersion in 1 M NaCl solution, Warburg impedances appeared in the medium frequency range (36 and 72 h of immersion, in Fig. 4 d). At this stage, the charge transfer resistance of the system decreased to about one-third of its initial value. When the immersion time increased to 144 h, the Warburg impedances appeared in the low frequency range. It can therefore be postulated that the corrosion process could be divided into three stages: the outer layer of the coating on the surface of the sample was destroyed and the electrolyte solution were transported through the inner layer at the initial stage of immersion (<18 h); at the second stage (18–144 h), the main reaction was the damage of inner layer; at the last stage (>144 h), the corrosion of the substrate played a dominant role. Equivalent circuits were also employed to explain the corrosion process. Results presented in Fig. 4 were fitted by using three equivalent circuits, corresponding to the aforementioned three stages. The equivalent circuit for the initial stage is presented in Fig. 5 a. It contains three time constants. The time constant in the high frequency domain is associated with the presence of the outer layer of the coating, the second constant in the intermediate frequency accounts for the presence of the inner layer, while the third constant in the low frequency corresponds to charge transfer reactions occurred on the substrate. In the equivalent circuit of Fig. 5 , the resistive elements R s , R f1 , R f2 and R ct represent the resistances of electrolyte, outer layer, inner layer and charge transfer, respectively. The capacitive elements C f and CPE f describe the properties of the protective layer, while C dl corresponds to the double layer capacity. The errors involved in the fitting procedures were under 10%. Constant phase element (CPE) is used most often to describe the frequency dependency of non-ideal capacitive characteristics [25,26] . The impedance of CPE is given by: (1) Z CPE = 1 Q ( j ω ) - n where j is the imaginary unit, ω is the angular frequency, Q corresponds to the pseudo capacitance of the coating and n is the depression angle (in degrees) that evaluates the semicircle deformation. The factor n , defined as a CPE power, is an adjustable parameter that always lies between 0.5 and 1. When n equals unity, the CPE describes an ideal capacitor. For 0.5 < n < 1, the CPE describes a distribution of dielectric relaxation times in frequency space. When n equals 0.5, the CPE represents a Warburg impedance with diffusional characteristics. Fig. 5 b–d displayed the fitting results in direct comparison with the experimental measurements shown earlier in Fig. 4 (20 min immersion time). The excellent agreement validates the model and the underlying corrosion mechanism. The detailed parameters used in the fitting are listed in Table 2 . It is apparent that with increasing immersion time, the coating resistances R f1 , R f2 and R ct initially increased and then decreased, whereas the opposite trend was observed for the capacitances C f and C dl . The changes in these physical properties reflect the changes taken place at the electrolyte/electrode interface during the immersion. In the initial stage of immersion (1 h), the gradual coverage of the corrosion product on electrode surfaces led to increases in R f1 , R f2 and R ct values. As the immersion time increase, ions in the electrolyte such as the chlorine ions infiltrated the La salt conversion coating through the micro-holes and other defects, and created more active points and defects in the process. The electrolyte infiltration facilitated the charge transfer process and thereby reduced the coating resistance. As a result, R f1 , R f2 and R ct values decreased with increasing immersion time. As the electrolyte permeated through the inner layer of the conversion coating and eventually reached the substrate/film interface, the exponents of CPE, n , gradually decreased to a value close to 0.5, indicating the presence of a diffusion field. In the corrosion process, the anodic reaction was the dissolution of zinc whereas cathodic reaction was predominantly the reduction of oxygen. The current density associated to the hydrogen discharge at the cathode is negligible compared to the current density related to oxygen reduction. Thus, the Warburg impedance could be attributed to oxygen transport from the bulk solution to the zinc surface [27] . The equivalent circuit for this stage of the corrosion process is presented in Fig. 6 a, where R s is the solution resistance, R f is the coating resistance, R ct is the charge transfer resistance, C f is the coating capacitance, CPE dl describes the non-ideal capacitive behavior of the substrate/film interface, W is the Warburg impedance associated to the oxygen diffusion process. Fig. 6 b–d display the results of the fitting to one set of the experimental measurements (36 h immersion time) presented in Fig. 4 . Excellent agreement was achieved, validating the adequacy of the model. The parameters used in the fitting are listed in Table 3 . During the third stage of corrosion, macro defects appeared in the coating, the transport process of chemical species proceeded without barriers. The diffusion field in the inner layer of the coating disappeared, while a new diffusion field appeared at the substrate/solution interface. At this stage, the coating offered no protection against corrosion, and the severe corrosion of the substrate commenced. The impedance spectra at the third stage ( Fig. 7 ) contain valuable information concerning the kinetics of the corrosion process occurring at the electrode surface. The equivalent circuit was again developed and the parameters for fitting are listed in Table 3 . In the range of high and intermediate frequencies, Nyquist plots exhibit a complex capacitive loop, which can be related to the active dissolution of zinc. While at low frequencies the impedance behavior reflects the transport process of reacting chemical species from solution to the electrode surface. 4 Conclusion The La conversion coating modified with citric acid on hot dip galvanized steel has an excellent corrosion performance in aerated 1 M NaCl solution. Electrochemical tests results show that the impedance value of modified La conversion coating is around 24 kΩ cm 2 , compared to only about 600 Ω cm 2 for bare HDG samples. R p of the coating tested by the potentiodynamic polarization curve is 26.84 kΩ cm 2 , approximately 50 times as bare HDG sample. The La salt conversion coatings inhibit both the anodic and cathodic responses of the system and hence prevent the HDG substrate from corrosion. The corrosion process of the coating can be divided into three stages. At the initial stage of immersion (<18 h), the outer layer of the coating on the surface of the sample was destroyed and the electrolyte solution were transport through the inner layer. At the second stage (18–144 h), the main reaction was the damage of inner layer. At the final stage (>144 h), the corrosion of the substrate played a dominant role. Acknowledgements The investigation is supported by the Fundamental Research Funds for the Central Universities ( 2009ZM 0072 ) and the ILZRO project ( ILZRO/IZA/2009023 ). The authors are also grateful to Dr. Daniel Liu from Teck PTC for the modification of English and several interesting discussions. References [1] B. Ramezanzadeh M.M. Attar M. Farzam Surf. Coat. Technol. 205 2010 874 884 [2] Abdel Salam Hamdy D.P. Butt A.A. Ismail Electrochim. Acta 52 2007 3310 3316 [3] Lihui Yang Junqing Li Xiang Yu Milin Zhang Xiaomei Huang Appl. Surf. Sci. 255 2008 2338 2341 [4] Daimon K. Heller William G. Fahrenholtz Matthew J. O’Keefe Corros. Sci. 52 2010 360 368 [5] Yingwei Song Dayong Shana Rongshi Chen Fan Zhang En-Hou Han Corros. Sci. 51 2009 62 69 [6] M.F. Montemor A.M. Simões M.G.S. Ferreira M.J. Carmezim Appl. Surf. Sci. 254 2008 1806 1814 [7] Gang Kong Jintang Lu Shuanghong Zhang Chunshan Che Haijiang Wu Surf. Coat. Technol. 205 2010 545 550 [8] B.R.W. Hinton L. Wilson Corros. Sci. 29 1989 967 975 [9] L. Roman M. Blidariu C. Cristescu Trans. Inst. Met. Finish. 75 1997 171 174 [10] K. Aramaki Corros. Sci. 46 2004 1565 1579 [11] Y. Hamlaoui F. Pedraza C. Remazeilles S. Cohendoz C. Rébéré L. Tifouti J. Creus Mater. Chem. Phys. 113 2009 650 657 [12] C. Motte N. Maury M.G. Olivier J.P. Petitjean J.F. Willem Surf. Film Technol. 200 2005 2366 2375 [13] M.A. Arenas J.J. de Damborenea Surf. Film Technol. 187 2004 320 325 [14] M.F. Montemor A.M. Simoes M.G.S. Ferreira Prog. Org. Films 44 2002 111 120 [15] Ajit Kumar Mishra R. Balasubramaniam Corros. Sci. 49 2007 1027 1044 [16] Jin Hu Shawei Tang Zaiyang Zhang Corros. Sci. 50 2008 3185 3192 [17] Luis M. Palomino Patrícia H. Suegama Idalina V. Aoki M.F. Montemor Hercílio G. De Melo Corros. Sci. 51 2009 1238 1250 [18] Luis M. Palomino Patrícia H. Suegama Idalina V. Aoki M. Fatima Montemor Hercílio G. De Melo Corros. Sci. 50 2008 1258 1266 [19] K. Aramaki Corros. Sci. 44 2002 2621 2634 [20] M.G.S. Ferreira R.G. Duarte M.F. Montemor A.M.P. Simões Electrochim. Acta 49 2004 2927 2935 [21] K. Aramaki Corros. Sci. 49 2007 1963 1980 [22] A. Tizpar Z. Ghasemi Appl. Surf. Sci. 252 2006 8630 8634 [23] A.S. Tselesh Thin Solid Films 516 2008 6253 6260 [24] Gang Kong Lingyan Liu Jintang Lu Chunshan Che Zheng Zhong J. Rare Earth 28 2010 461 465 [25] G. Quartarone M. Battilana L. Bonaldo T. Tortato Corros. Sci. 50 2008 3467 3474 [26] Y.X. Qiao Y.G. Zheng W. Ke P.C. Okafor Corros. Sci. 51 2009 979 986 [27] H. Ma S. Chen B. Yin S. Zhao X. Liu Corros. Sci. 45 2003 867 882