Abstract:A simple and economical one-pot method to synthesize high-quality water soluble CdTe QDs is reported. An 83% quantum yield (QY) was reached using TGA as the ligand in aqueous solution without protection of nitrogen gas when using K2TeO3 as a stable Te source and NaBH4 as reducing agent. The size of the CdTe NCs could be tuned by the duration of reflux and easily monitored by absorption and PL spectra. At the optimum conditions (pH = 10.5, the concentration of Cd2+ was 1.0 mmol l(-1) and the ratio of Cd2+ : Te2- : TGA : NaBH4 was 1 : 0.2 : 1 : 10), the maximal QY reached 83%, which was much higher than that of samples prepared by the traditional refluxing aqueous solution method. The X-ray diffraction (XRD) patterns indicated that CdS was formed in the preparation process of CdTe NCs. This CdS shell could effectively passivate the surface trap states, and enhance the PL QY and stability of the CdTe QDs. The temporal evolution of the absorption spectrum of thioglycolic acid indicated that TGA was decomposed and released S2- during the preparation of CdTe QDs. The S2- reacted with Cd2+ to form CdS, this is consistent with the XRD results. 3-Mercaptopropionic acid (MPA) was also used as a ligand in this system and the results indicate that high quality multi colour CdTe NCs could also be obtained using MPA as the ligand. By this simple method, there is no need of N-2 protection, buffering solution, special ligands, large quantity of N2H4 or particular treatment (such as microwave, or ultrasonication).

Significant Enhancement of the Quantum Yield of CdTe Nanocrystals Synthesized in Aqueous Phase by Controlling the Ph and Concentrations of Precursor Solutions

Aqueous Synthesis of Highly Luminescent CdTe Quantum Dots and Its Growth Mechanism

Controlling the fluorescent properties of aqueous CdTe nanocrystals by modulating the growth rate.

Aqueous Synthesis of CdTe/CdS/ZnS Quantum Dots and Their Optical and Chemical Properties

Aqueous synthesis of highly monodispersed thiol-capped CdTe quantum dots through electrochemical approach.

A simple and economical one-pot method to synthesize high-quality water soluble CdTe QDs

Synthesis of Positively Charged Luminescent Cdte Nanocrystals in Aqueous Solution

Simple Synthesis of Highly Luminescent Water-Soluble CdTe Quantum Dots with Controllable Surface Functionality

Synthesis of Highly Luminescent Mercaptosuccinic Acid-Coated Cdse Nanocrystals under Atmospheric Conditions

An Improved One-Pot Aqueous Phase Synthesis Of Cdte Qds

Synthesis of Aqueous Cdte Nanocrystals with High Efficient Blue-Green Emission of Exciton

Rapid Aqueous Synthesis of High-quality CdTe Colloidal Quantum Dots

Facile One-Step Photochemical Synthesis of Water Soluble Cdte(S) Nanocrystals with High Quantum Yields

Synthesis and Characterization of High Quantum Yield CdTe Quantum Dots in Aqueous Phase

Stoichiometric Ratio Dependent Photoluminescence Quantum Yields of the Thiol Capping CdTe Nanocrystals

Synthesis of CdTe Colloidal Quantum Dots (qds) in Water

Selective Synthesis of CdTe and High Luminescence CdTe/CdS Quantum Dots: the Effect of Ligands.

Synthesis and Bio-Imaging Application of Highly Luminescent Mercaptosuccinic Acid-Coated CdTe Nanocrystals

Preparation of water-soluble CdTe/CdS core/shell quantum dots with enhanced photostability

Controllable Aqueous Synthesis and Characterization of Stable CdTe Nanocrystals

Aqueous Phase Synthesis of CdTe Quantum Dots for Biophotonics