The effect of icariin on growth and ECM secretion of chondrocytes cultured in collagen scaffold

Zhang Xuan,Xiao Yumei,Wang Ru,Li Dongxiao,Fan Hongsong,Zhang Xingdong

DOI: https://doi.org/10.13412/j.cnki.zyyl.2010.06.009

2010-01-01

Abstract:Objective: In order to provide experimental foundation for application of icariin(Ica) to cartilage tissue engineering,the effect of icariin on the proliferation,morphology and ECM secretion of rabbit cartilage chondrocytes cultured in 2D and 3D conditions was evaluated.Methods :Rabbit chondrocytes were isolated from articular cartilage and cultured in medium containing α-MEM.The chondrocytes were seeded onto sterilized Ica/Col films and the morphology of cells cultured for 2 days was visualized using inverted fluorescence microscope.MTT method was used to examine the effect of Ica on cell proliferation.Chondrocytes-Ica/Col constructs were prepared and cultured under static conditions in a humidified atmosphere with 5% CO2 at 37℃.The chondrocytes cultured in hydrogel constructs were observed by confocal laser scanning microscopy to evaluate the cytocompatibility of hydrogels.HE,toluidine blue staining and biochemical assays were employed to evaluate the effect of Ica on ECM secretion of chondrocytes.Results: The chondrocytes cultured on Ica/Col films showed good cell morphology and higher proliferation compared to Col films after cultured for 6days,suggesting no obvious cytotoxicity of icariin toward chondrocytes.The amount of chondrocytes appeared the tendency of clustered growth in the Ica/Col hydrogel constructs was more than that of in Col hydrogel constructs and the clustering cells possessed spherical morphology similar as the cells in normal cartilage.And the Ica/Col hydrogels improved rabbit chondrocytes secreting the ECM compared with the collagen hydrogels,suggesting that Ica could promote chondrocytes secreting ECM.Conclusion: icariin had good biocompatibility to chondrocytes and could maintain the chondrocytic phenotype and promot the cell secreting ECM.Ica had potential to be used as an accelerant for cartilage tissue engineering.