Abstract:Ag nanoparticles (NPs) were uniformly immobilized in hierarchically porous monolithic silica using. gamma-(aminopropyl) triethoxysilane (APTES) as a modifier and ethanol as a reductant, where the silica monolith was pre-prepared via the sol-gel accompanied by phase separation. Ag NPs embedded in the hierarchically porous silica monoliths were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), mercury porosimetry, nitrogen adsorption/desorption analysis, and X-ray photoelectron spectroscopy (XPS). The mechanism of the modification by APTES, the reduction using ethanol, and pore structure changes of the silica monolith after immobilization of Ag NPs are discussed. The results show that APTES modifies the monolith by incorporating amino groups onto the surface of the meso-macroporous skeletons, and then amino groups react with silver ions to form a silver-amine complex. Ethanol used as an effective reductant is adopted to promote the reduction process of the silver-amine complex. Ag NPs with an average size of approximately 16 nm were homogeneously supported on both the macroporous skeletons and in the mesopores of the silica monolith with good dispersion. The embedding of Ag NPs did not spoil the macroporous skeleton of the monolithic silica, and the surface area decreased from 418 to 254 m(2).g(-1) after introducing Ag NPs into its macro-mesopores. It was also found that the loading amount of Ag NPs increased with repeated modification and reduction treatments.

Step-by-Step Synthesis of Silver Nanoparticles and Their Surface Modification

Preparation of Silver Nanoshells on Silica Particles by a Simple Two-step Process

Preparation and Microstructure of Silver Nanopowder with Spheric Morphology

Synthesis and Characterization of Silica–silver Core–shell Composite Particles with Uniform Thin Silver Layers

Morphology and Composition Controlled Synthesis of Flower-Like Silver Nanostructures.

A Review on Diverse Silver Nanostructures

Preparation and Characterization of Silver Coated Hollow SnO2 Sphere with Open Structure

Colloidosome-Based Synthesis Of A Multifunctional Nanostructure Of Silver And Hollow Iron Oxide Nanoparticles

A Facile Synthetic Route to Aqueous Dispersions of Silver Nanoparticles

Preparation of Silver-Coated Polystyrene Composite Particles

A Facile Synthesis of Silver-Coated Composite Particles by Swelling Surface Method

Preparation of Ag-Al2O3 nano-composites powder

Seedless and electroless plating of silver on silica particles by using microreactor

Preparation and characterization of silica–silver core-shell structural submicrometer spheres

Fabrication and characterization of silver core and porous silica shell nanocomposite particles

Silver Nanoparticle Generators: Silicon Dioxide Microspheres.

An Improved Seed-Mediated Growth Method to Coat Complete Silver Shells Onto Silica Spheres for Surface-Enhanced Raman Scattering

Preparation and Characterization of Ag Nanoparticles Embedded in Hierarchically Porous Monolithic Silica

A Facile One-Pot Synthesis of Uniform Core-Shell Silver Nanoparticle@mesoporous Silica Nanospheres.

Fabrication of nanoscaled silica layer on the surfaces of submicron SiO2-Ag core-shell spheres

Ag@C Core/shell Structured Nanoparticles: Controlled Synthesis, Characterization, and Assembly.