Enhanced fluoride remediation from aqueous solution by La-modified ZIF-8 hybrids
Weisen Yang,Wenlong Jiang,Fengshuo Shi,Yifei Liu,Yuhuang Chen,Gaigai Duan,Chunmei Zhang,Jiapeng Hu,Shaoju Jian
DOI: https://doi.org/10.1016/j.colsurfa.2023.131726
2023-05-27
Abstract:To ensure water safety, fluoride elimination from aqueous environment is an urgent affair. In this study, a series of La-modified ZIF-8 (denoted as La-ZIF-8) hybrids with different contents of La were fabricated via a solvothermal reaction and used for fluoride recovery from wastewater. The structure and morphology of the fabricated La-ZIF-8 hybrid were confirmed by various techniques (SEM, XRD, BET, FTIR, and XPS). The specific surface area along with the pore volume of La-ZIF-8 hybrid was 121 m 2 g −1 and 0.816 cm 3 g −1 , respectively. The defluoridation performance of La-ZIF-8 under different conditions was assessed by static batch trials. The optimized La-ZIF-8 with a La/Zn molar ratio of 4:1 achieved the supreme defluoridation performance. The fluoride uptake was greatly enhanced from 1.85 mg g −1 for pure ZIF-8–49.5 mg g −1 for La-ZIF-8 at C 0 = 10 mg L −1 . The results revealed that La-ZIF-8 had a maximal fluoride uptake of 224.72–230.95 mg g −1 at 30–50 °C, pH 4, and C 0 = 80 mg L −1 . Adsorption of fluoride on La-ZIF-8 obeyed to the Langmuir isotherm ( R 2 > 0.99) and pseudo-second order model ( R 2 > 0.999), reflecting a single-layer chemical adsorption process. Δ H 0 (36.38 kJ mol −1 ) > 0, Δ S 0 (155.36 J mol −1 K −1 ) > 0, and Δ G 0 < 0 stated that the defluoridation by La-ZIF-8 is an endothermic nature, random state, highly feasible and spontaneous process. The co-existing of cations and anions effect inferred that Mg 2+ , Ca 2+ , SO 4 2– , Cl – , and NO 3 – only had a trivial impact on fluoride removal performance, illustrating the high selectivity for F – . The La-ZIF-8 can be deemed to be a candidate adsorbent for tackling F − pollution
chemistry, physical