Abstract:Nanocrystalline ZnO films were grown on silicon substrate by hydrothermal synthesis at 125 °C, using diethanolamine as additive. A powder containing ZnO spheres, with diameters between 100 to 200 nm and formed by aggregation of ZnO nanoparticles, was also obtained as a secondary reaction product. The samples were studied by scanning electron microscopy, X-ray diffraction and photoluminescence (PL) spectroscopy. The effects of the [diethanolamine]/[Zn2+] molar ratio on morphological, structural and optical properties were studied, as well as the effect of laser illumination (λ = 325 nm) and annealing treatment on photoluminescence properties. The film samples exhibited a compact columnar structure, with thickness between 180 to 210 nm, which were not strongly affected by the diethanolamine concentration. The X-ray diffraction patterns from the films evidenced preferred orientation along the c-axis of the ZnO wurzite structure; while the nanospheres did not show any preferential crystalline direction. The PL spectra from the films showed large initial UV emission and a weak defect band centered in the yellow. A PL evolution while the samples were UV illuminated was observed. The relaxation of metastable phases (formed during the low temperature growth) involving the creation of point defects, is suggested. The predominance of the yellow defect band before and after treatment points at oxygen vacancies as the possible point-defect candidate.

Growth of Dumbbell-Like ZnO Microcrystals under Mild Conditions and Their Photoluminescence Properties.

Synthesis of Two-Dimensional Micron-Sized Single-Crystalline ZnS Thin Nanosheets and Their Photoluminescence Properties

Synthetic and Effect of Annealing on the Luminescent Properties of Zno Nanowire

Preparation of ZnO Particle with Novel Nut-Like Morphology by Ultrasonic Pretreatment and Its Luminescence Property

Effect of Solution Concentrations on Crystal Structure, Surface Topographies and Photoluminescence Properties of ZnO Thin Films

Preparation And Characterization Of Dumb-Bell Zno

Low-temperature growth of uniform ZnO particles with controllable ellipsoidal morphologies and characteristic luminescence patterns.

Preparation and Photoluminescence of ZnO with Nanostructure by Hollow-Cathode Discharge

Morphology Investigation of Hydrothermally Prepared ZnO Micro-Crystals Influenced by Cu2+ Ions

The synthesis of novel ZnO microcrystals through a simple solvothermal method and their optical properties

Synthesis and electromagnetic characteristics of ZnO micro-crystal with varying morphology

Photoluminescence Characterization of Nanocrystalline ZnO Array

Growth And Characterization Of Cu-Catalyzed Zno Nanowires

Controllable Growth of ZnO Microcrystals by a Capping-Molecule-Assisted Hydrothermal Process

Novel ZnO microballs synthesized via pyrolysis of zinc-acetate in oxygen atmosphere

Benzenedicarboxylic Acid-Assisted Synthesis of ZnO Micro-Hexagons from Zinc Hydroxide Nanostrands and Their Photoluminescence Properties

Straight and Thin ZnO Nanorods: Hectogram-Scale Synthesis at Low Temperature and Cathodoluminescence.

Facile Solution Synthesis and Characterization of Zno Mesocrystals and Ultralong Nanowires from Layered Basic Zinc Salt Precursor

Synthesis of ZnO Eggshell-Like Hollow Spheres Via Thermal Evaporation at Low Temperature

Growth Of Zno Crystals With Branched Spindles And Prismatic Whiskers From Zn-3(Oh)(2)V2o7 Center Dot H2o Nanosheets By A Hydrothermal Route

Metastability effects on the photoluminescence of ZnO nano-micro structures grown at low temperature and influence of the precursors on their morphology and structure