Effect and Enhancement of Forging Action During Friction Stir Welding

ZHANG Gui-feng,SU Wei,ZHANG Jun,ZHANG Jian-xun

DOI: https://doi.org/10.3969/j.issn.1001-2303.2011.01.010

2011-01-01

Abstract:To visualize the fact that the forging effect can be enhanced by tilting tool during friction stir welding,a novel experimental way,in which a backing plate with predrilled hole was used,was proposed and expected result was obtained.Using a tool without pin and a backing plate with a predrilled hole(φ4 mm) the friction lap welding of 2 mm thick aluminum sheet was performed under the conditions of tilting tool(3°) and not tilting tool(0°).The length of plasticized aluminum extruded into predrilled hole within backing plate was 5.3 mm and 2.6 mm at different tilting angle of 3° and 0°,respectively.The result indicated that the forging effect can be enhanced by tilting tool,the primary loaded body of forging effect should be plasticized material at trading edge of pin(but beneath shoulder),and the primary loading body of forging effect should be shoulder especially when using smooth pin without thread.Based on the above result,a mathematical relationship between axial forging pressure and tilt angle was proposed.It was derived from the mathematical relationship and comparative result of defect in the two kinds of welds with and without tilt angle that he forging effect has significant contribution to eliminating void defect behind pin due to the enhancement of plastic flow in multi-directions,especially in axial direction of tool.