Prediction of Location of Fretting Fatigue Crack Initiation Subject to High Stress Ratio Cyclic Load

ZHANG Shao-yun,QIAN Zhi-hong,TAO Wei-ming

DOI: https://doi.org/10.3969/j.issn.0254-0053.2013.02.008

2013-01-01

Abstract:For fretting fatigue problems,the stress ratio of cyclic load can greatly affect the stress state and distributions as well as the location of fatigue crack initiation.Based on finite element analysis for a kind of fretting fatigue problem,the fretting fatigue test was simulated,and the maximum tangential stress range Δσθmax was used as the criterion value to predict the location of fatigue crack initiation under different stress ratio cyclic load.When the stress ratio is not very high,numerical results show that the specimen get contact with the edge of the pad.Therefore there are severe stress concentrations at that position and fatigue cracks are prone to onset.On the other hand,the edge of the pad keeps separate from the specimen surface when stress ratio is high enough,and the maximum stress range Δσθmax as well as fatigue crack initiation displace at a distance from the edge of initial contact.The predicted crack initiation locations are in agreement with those from experiments.