Abstract:Well-ordered two-dimensional (2D) hexagonal periodic mesoporous organosilicas (PMOs) with a high content of disulfide groups have been prepared by a simple metal-ions-assisted amphiphilic surfactant templating process under a strong acidic condition. Long-chain organic bridge silane, bis(triethoxysilylpropyl)disulfide (BTSPDS) was used as a precursor which can be co-condensed with tetraethoxysilane (TEOS) to assemble with the triblock copolymer Pluronic P123 template and to construct the mesostructured organic–inorganic frameworks. The content of disulfide functional groups is up to 20% (BTSPDS molar content in the initial silane mixture) incorporated into the framework. The obtained ordered mesoporous DS-PMO materials have relatively high BET surface area (∼580m2/g), large uniform pore size (up to 6.3nm) and thick pore walls (thickness up to 7.1nm), because of the long-chain disulfide bridges. The metal ions such as Zn2+ formed the four-coordination complex with two sulfides of BTSPDS and ethylene oxide moieties of P123 template, which could enhance the interaction between the “soft” long disulfide groups and P123 template, thus improving the mesostructural regularity correspondingly. The disulfide-bridged PMO materials exhibit excellent hydrothermal stability in boiling water for 5 days, probably due to the thick pore walls. SEM images show that after the hydrothermal treatment, the morphology of the ordered disulfide-bridged PMO materials is retained, as that of the wheat-like SBA-15. Excellent adsorption efficiency (∼716mg/g) for Hg2+ ions is observed, suggesting a potential application in removal of heavy metal ions in wastewater.

Periodic Mesoporous Organosilicas with Chiral Mn(Ⅲ) Salen Prepared through Co-condensation Method

Synthesis and characterization of periodic mesoporous organosilica with various morphologies

Chiral norbornane-bridged periodic mesoporous organosilicas

Mesoporous Silicas Functionalized with Aminopropyl Via Co-Condensation: Effective Supports for Chiral Mn(III) Salen Complex

Periodic Mesoporous Organosilica Materials: Self-Assembly of Carbamothioic Acid-Bridged Organosilane Precursors.

Mesostructure-controlled synthesis of chiral norbornane-bridged periodic mesoporous organosilicas

Preparation and Catalytic Activity of Periodic Mesoporous Organosilica Incorporating Lewis Acidic Chloroindate(iii) Ionic Liquid Moieties

Periodic mesoporous organosilicas with helical and concentric circular pore architectures.

Mesoporous Silica Supported Unsymmetric Chiral Mn(III) Salen Complex: Synthesis, Characterization and Effect of Pore Size on Catalytic Performance

Functionalized Periodic Mesoporous Organosilicas: Hierarchical and Chiral Materials

Templated Synthesis of Electroactive Periodic Mesoporous Organosilica Bridged with Oligoaniline.

Synthesis of Large-Pore Urea-Bridged Periodic Mesoporous Organosilicas

Synthesis of Ordered Cubic Periodic Mesoporous Organosilicas with Ultra-Large Pores

(R)-(+)-binol-functionalized Mesoporous Organosilica As A Highly Efficient Pre-Chiral Catalyst for Asymmetric Catalysis

Synthesis of Periodic Mesoporous Organosilicas with Chemically Active Bridging Groups and High Loadings of Thiol Groups

Synthesis, Bifunctionalization, and Application of Isocyanurate-Based Periodic Mesoporous Organosilicas

Progress in Functionalization and Application of Periodic Mesoporous Organosilicas

A Metal-Ion-assisted Assembly Approach to Synthesize Disulfide-Bridged Periodical Mesoporous Organosilicas with High Sulfide Contents and Efficient Adsorption

Highly ordered periodic mesoporous organosilica nanoparticles with controllable pore structures

A novel strategy to prepare PMOs with high loading of organic species by releasing organic precursor

Manipulation of the phase structure of vinyl-functionalized phenylene bridging periodic mesoporous organosilica