La0.67(Ca0.24Sr0.09)MnO3:xAg2O (0 ≤ X ≤ 0.25) Composites with Improved Room–temperature TCR and MR for Advanced Uncooling Infrared Bolometers and Magnetic Sensors
Tao Sun,Yang Liu,Gang Dong,Shuai Zhang,Zhidong Li,Kaili Chu,Xingrui Pu,Hongjiang Li,Fuquan Ji,Hui Zhang,Qingming Chen,Xiang Liu
DOI: https://doi.org/10.1016/j.apsusc.2019.07.056
IF: 6.7
2019-01-01
Applied Surface Science
Abstract:In this research, high-density La-0.67(Ca0.24Sr0.09)MnO3:xAg(2)O (LCSMO: xAg(2)O, x = 0, 0.05, 0.1. 0.15, 0.2, and 0.25) composites were successfully fabricated through the conventional sol-gel method. Scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and XRD data confirmed presence of silver at A sites (La3+/Ca2+/Sr2+) as Ag+ and segregates at grain boundaries (GBs) to form metallic silver. The electrical properties greatly improved by adding Ag2O. Significant enhancements in peak temperature coefficient of resistivity (TCR) and magnetoresistance (MR) at room-temperature (300 K) were observed for LCSMO:xAg(2)O composites. The peak TCR increased from 3.7% K-1 (299.3 K, for x = 0) to 14.8% K-1 (301.0 K, for x = 0.2), and MR rose from 16.9% (303.0 K, for x = 0) to 34.1% (300.6 K, for x = 0.2). These improvements in peak TCR were attributed to increased grain size and formation of metallic silver at GBs or within the composites. Moreover, peak MR was higher in Ag2O doped composites, which was mainly due to large spin polarization effect and strong coupling ferromagnetic domains under external magnetic field. Overall, the large room-temperature TCR and MR values of LCSMO:0.2Ag(2)O composites look promising for future advanced uncooling infrared bolometers and magnetic sensors.