Modulation and Stabilization of Silk Fibroin-Coated Oil-In-Water Emulsions

Jia-Jia Rao,Zhong-Min Chen,Bing-Can Chen

2009-01-01

Food Technology and Biotechnology

Abstract:The purpose Of this study is to prepare and characterize stable oil-m-water emulsions containing droplets coated with silk fibroin Silk fibroin, a native edible fibrous protein on.-mating from silkworm cocoons, was Used to prepare 10 % (by mass) corn oil-in-water emulsions at ambient temperature (pH=7.0, 1.0 mM phosphate buffer) Emulsions With relatively small mean particle diameter (d(32)=047 mu m) and extremely good creaming stability (>7 days) could be produced at silk fibroin concentration of 1 % (by mass) The influence of pH (2-8), thermal processing (60-90 degrees C, 20 mm), and concentration of salt (c(NaCl)=0-250 mM) on the properties and stability of the emulsions was analyzed using zeta-potential, particle size, and creaming stability measurements The isoelectric Point of droplets stabilized with silk fibroin was pH similar to 4 The emulsions were stable to droplet flocculation and creaming at any pH except intermediate value (pH=4 0) when stored at room temperature, which was attributed to their relatively low zeta-potential. Their zeta-potential went from around 25 to -35 mV as the pH was increased from 2 to 8 The emulsions were also stable to thermal treatment (60 and 90 degrees C for 20 mm, pH=3 and 7), with a slight decrease in the magnitude of zeta-potential it temperatures exceeding 60 degrees C The emulsions were Unstable to aggregation and creaming even at relatively low salt concentrations (c(NaCl)=0-250 mM, pH=3 and 7) as a result of electrostatic screening effects These results suggest that bulk oil stabilized with silk fibroin has improved physical stability and may provide a new way of creating functional oil products and delivery systems.