Electrochemical Properties of La0.8Sr0.2FeO3-δ Based Composite Cathode for Intermediate Temperature SOFC

Zhang Naiqing,Sun Kening,Ra Dechang,Zhou Derui

DOI: https://doi.org/10.1016/s1001-0521(07)60112-0

2006-01-01

Abstract:La0.8Sr0.2FeO3-delta is a new kind of cathode material for intermediate SOFC, but its electrochemical activity is relative poor for the lanthanum gallate based solid oxide fuel cell. In this paper, a novel composite cathode of La0.8Sr0.2FeO3-delta/La0.9Sr0.1Ga0.8Mg0.2O3-delta was prepared on the LSGM electrolyte substrate by screen-printing method. The results of cathodic polarization measurements show that the overpotential decreases significantly when the composite cathode is used instead of the La0.8Sr0.2FeO3-delta single layer cathode. The cathodic overpotential of the composite La0.8Sr0.2FeO3-delta/La0.9Sr0.1Ga0.8Mg0.2O3-delta cathode is 150 mV at the current density of 0.2 A center dot cm(-2) at 800 degrees C, while the cathodic overpotential of the La0.8Sr0.2 FeO3-delta single layer cathode is higher than 260 mV at the same condition. The electrochemical impedance spectroscopy was employed to investigate the polarization resistance of the cathode. The polarization resistance of the composite cathode is 1.20 Omega center dot cm(2) in open circuit condition, while the value of the single Lao,8 Sr0.2FeO3-delta cathode is 1.235 Omega center dot cm(2).