Abstract:In this study, standard test specimens with flame‐retarded short glass fiber‐reinforced PC/ABS materials were fabricated under rapid thermal cycle injection molding condition by selecting a potassium perfluorobutane sulfonate flame retardant specially used for PC, FR2025, and two kinds of aryl phosphorus halogen‐free flame retardants, UN707 and PX‐220. The flame‐retardancy effect of the above different flame retardants on the studied systems was compared through combustion tests of the specimens. Meanwhile, the thermal and mechanical properties of flame‐retarded composites were studied by using the thermogravimetry analysis, dynamic mechanical thermal analysis (DMTA), and universal testing machine. The results show that the “candlewick effect” of fibers exacerbates the fire behavior of composites. With the increase of the aryl phosphorus halogen‐free flame retardants, the flame‐retardancy effect of composites is obviously improved, and the maximum thermal degradation rate of composites is significantly decreased. The UL94 combustion rating is improved, and the time of residual flame is substantially reduced with the increase of PC content under the same content of flame retardant. The DMTA results show that the flame retardants have a reinforcement action on PC/ABS matrix. However, the macroscopic mechanical properties are slightly decreased in the glass fiber‐reinforced composites because of the destructive effect of the flame retardants on the interface compatibility between matrix and fibers; the scanning electron microscopic micrographs of tensile fracture fully prove this action mechanism of flame retardants. In addition, the addition of toughener and antidripping additive significantly affects the flame retardancy and mechanical properties of composites. POLYM. COMPOS., 36:1653–1663, 2015. © 2014 Society of Plastics Engineers

Study on Thermal Decomposition Kinetics of Flame Retarded PC by Potassium Perfluorobutane Sulfonate

Mechanical Properties and Thermal Degradation of Flame Retardant PC/HDPE Blending with Spirocyclic Hydroxybenzene Phosphate

Thermal Degradation Behaviours of Flame-Retardant Polycarbonate Containing Potassium Diphenyl Sulfonate and Polymethylphenylsilsesquioxane

Study onKinetics of Flame Retardant of Thermal Degradation Polyphosphate

Thermal Degradation Behavior and Flame Retardancy of Polycarbonate Containing Poly[(phenylsilsesquioxane)-co-(dimethylsiloxane)] and Potassium Diphenyl Sulfonate

Thermal degradation behavior of low-halogen flame retardant PC/PPFBS/PDMS

Thermal Clegeadation Kinetics of Flame Retarded PC/ABS

Thermal oxidative degradation kinetics of flame-retarded polypropylene with intumescent flame-retardant master batches in situ prepared in twin-screw extruder

Thermal behaviors of flame-retardant polycarbonates containing diphenyl sulfonate and poly(sulfonyl phenylene phosphonate)

Kinetics of Thermal Oxidative Degradation of Phosphorus-Containing Flame Retardant Copolyesters

Kinetics Study of Thermal Decomposition of Epoxy Resins Containing Flame Retardant Components

Investigation on Phosphorus Halogen‐free Flame‐retardancy Systems in Short Glass Fiber‐reinforced PC/ABS Composites under Rapid Thermal Cycle Molding Process Condition

The Kinetics of Thermal Degradation of A Halogen-Free Flame-Retarded Polypropylene

Thermal Degradation Kinetics of Halogen-Free Flame-Retarded Polyethylene Composites

Study on Thermal Decomposition Kinetic of Pa6 Flame-Retarded by Brominated Polystyrene Synchronized with Antimony Trioxide

Thermal oxidative degradation kinetics of novel intumescent flame-retardant polypropylene composites

Study on Flame-Retardant Mechanism of Polycarbonate Containing Sulfonate-Silsesquioxane-fluoro Retardants by TGA and FTIR

Study on Synergistic Effect of Perfluorsulfonate and Polysiloxane Flame Retardants in Polycarbonate

Flame Retardant and Thermal Pyrolytic Behaviour of PP Flame-Retarded with MPP/PER/P System

STUDY ON KINETIC OF THERMAL DEGRADATION OF FLAME RETARDANT COPOLYESTERS——Ⅰ.THE COMPARISION BETWEEN PHOSPHORUS-CONTAINING COPOLYESTER AND PET

Thermal Degradation Kinetics and Lifetime Estimation for Polycarbonate/polymethylphenylsilsesquioxane Composite