Photoluminescence Properties of YVO_4:Eu~(3+) Phosphor after Thermal Treatment
ZUO Yin-yan,LING Wei-jun,ZHANG Feng,GAO Hui,WANG Yu-hua
2010-01-01
Chinese Journal of Luminescence
Abstract:YVO4:Eu3+ was successfully synthesized by hydrothermal method,and was further thermally treated at 400 ～ 800 ℃,respectively.Their crystal structure,SEM(scanning electron microscope)images and luminescence properties were obtained in room temperature.XRD showed that YVO4:Eu3 + was formed with good single phase,and when the temperature changes in 400 ～ 800 ℃,the crystallinity is higher and higher,and the crystal grain become bigger and bigger than untreated sample.SEM images also indicated the grain of the sample after treatment is bigger than that of YVO4:Eu3 + before treatment.In the UV range,the excitation band is composed of a broad band with the maximum at about 260 nm and a sharp band with the maximum at about 395 nm.The peak of 260 nm is assigned to the overlap of VO43-ion and O2-→Eu3 + charge transfer band absorption;the peak at 395 nm is due to 7F0→5L6 transition of Eu3 +.In the VUV range,the excitation band was composed of a strong broad band at about 156 nm and a broad band at about 200 nm.The peak of 156 nm could be assigned to the absorption band of host,and the peak of 200 nm is assigned to the charge transfer band of O2-→Y3 +.After 200 nm,the shape of absorption spetrum is similar to the UV excitation spectra.under 254 nm excitation,the YVO4:Eu3 + phosphor exhibits the well-known Eu3 + emission,which makes up of several sharp lines of Eu3 +,namely the 5D0→7F1,5D0→7F2,5D0→7F4 transitions,respectively,the dominated emission peak is 5D0→7F2 at 619 nm under 147 nm excitation,their emission spectra are consistent with that under 254 nm excitation.With the temperature increasing in 400 ～ 800 ℃,the emission intensity of samples is improved because of the higher crystallinity,bigger grain,and removing of OH-and VO34-which can quench the luminescence.Under 254 nm and 147 nm excitation,the emission intensity of the sample thermally treated at 800 ℃ is improved 90% and 95% comparing with the untreated sample,respectively.It was indicated that 800 ℃ is the best thermal treatment temperature.