Crystal Growth, Spectral Properties and Continuous Wave Laser Operation of New Mixed Nd:GdYNbO4 Laser Crystal
Shoujun Ding,Qingli Zhang,Fang Peng,Wenpeng Liu,Jianqiao Luo,Renqin Dou,Guihua Sun,Xiaofei Wang,Dunlu Sun
DOI: https://doi.org/10.1016/j.jallcom.2016.12.263
IF: 6.2
2016-01-01
Journal of Alloys and Compounds
Abstract:A new mixed laser crystal Nd:Gd0.69Y0.3NbO4 (Nd:GYNO) with high quality was grown successfully by Czochralski method. Its structure parameters are obtained by the X-ray Rietveld refinement method. The effective segregation coefficient of Nd3+ ions is 0.61 in GYNO host. The maximum absorption cross section at 809 nm and peak emission cross section at 1065.6 nm of Nd: GYNO crystal are 11.6 x 10(-20) and 20.5 x 10(-20) cm(2), respectively. The fluorescence lifetime of F-4(3/2) manifold for Nd3+ in Nd:GYNO crystal is fitted to be 156 mu s. Diode-pumped continuous-wave laser operations at 1.06 mu m with Nd: GYNO crystals cut perpendicular to crystallographic a, b, and c axes (denoted as a-, b-c-cut, respectively) were demonstrated. A maximum output power of 0.98 W was obtained with c-cut crystal, corresponding to an optical-to-optical conversion efficiency of 31.3% and a slope efficiency of 30.4%. All these results imply that the Nd: GYNO crystal has great potential application in low and even moderate lasers. (C) 2016 Elsevier B.V. All rights reserved.