Synthesis and properties of organic silicone modified acrylate nanolatexes with high solid content

Zhang Qingxuan,Yang Pujiang,Gao Ying,Zhou Zhaohui,Yang Guohua,Wang Zongxian

DOI: https://doi.org/10.3969/j.issn.1000-1255.2006.06.004

2006-01-01

Abstract:Organic silicone modified acrylate nanolatexes with 59.8 nm of average particle size, narrow size distribution and mass fraction of solid 40% were prepared by semi-continuous monomer addition method with emulsifier mixtures of anionic emulsifier sodium dodeoyl sulfate(SDS), nonionic emulsifier polyoxyethylene octylphenol ether (OP-10), reactive anionic emulsifier WH-100 and nonionic wetting agent. The properties of the nanolatexes and their films were studied. The results showed that the Ca~ 2+ stability of the nanolatexes and water absorption of their films prepared by semi-continuous monomer addition method were less than that of latexes prepared by batch pre-emulsification method, but gel contents were approximately equal.The conversions changed slightly, Ca~ 2+ stability and water absorption decreased and particle size increased with increasing organic silicone vinyltriethoxysilane (A 151) amount. Optimized mass fraction of organic silicone in recipe was 4%. The Ca~ 2+ stability first increased then decreased and water absorption decreased then increased with the increasing functional monomer 2-hydroxyethyl methacrylate(HEMA) amount. The optimized mass fraction of HEMA in recipe was less than 3%.