Abstract:The fatigue fracture behavior of four ultrahigh strength steels with different melting processes and therefore different inclusion sizes were studied by using a rotating bar two-point bending fatigue machine in the high-cycle regime Up to 10(7) cycles of loading. The fracture surfaces were observed by field emission scanning electron microscopy (FESEM). It was found that the size of inclusion has significant effect on the fatigue behavior. For AISI 4340 steel in which the inclusion size is smaller than 5.5 mu m, all the fatigue cracks except one did not initiated from inclusion but from specimen surface and conventional S-N curve exists. For 65Si2MnWE and Aermet 100 steels in which the average inclusion sizes are 12.2 and 14.9 mu m, respectively, fatigue cracks initiated from inclusions at lower stress amplitudes and stepwise S-N curves were observed. The S-N curve displays a continuous decline and fatigue failures originated from large oxide inclusion for 60Si2CrVA steel in which the average inclusion size is 44.4 mu m. In the case of internal inclusion-induced fractures at cycles beyond about 1x10(6) for 65Si2MnWE and 60Si2CrVA steels, inclusion was always found inside the fish-eye and a granular bright facet (GBF) was observed in the vicinity around the inclusion. The GBF sizes increase with increasing the number of cycles to failure N-f in the long-life regime. The values of stress intensity factor range at crack initiation site for the GBF are almost constant with N-f, and are almost equal to that for the surface inclusion and the internal inclusion at cycles lower than about 1x10(6). Neither fish-eye nor GBF was observed for Aermet 100 steel in the present study.

ESTIMATION OF THE CRITICAL SIZE OF INCLUSION IN HIGH STRENGTH STEEL UNDER HIGH CYCLE FATIGUE CONDITION

On the critical inclusion size of high strength steels under ultra-high cycle fatigue

A Modified Coffin-Manson Model for Ultra-Low Cycle Fatigue Fracture of Structural Steels Considering the Effect of Stress Triaxiality

Study on the Prediction Method of the Ultra-Low-Cycle Fatigue Damage of Steel

Improved Ultra-Low Cycle Fatigue Fracture Models for Structural Steels Considering the Dependence of Cyclic Damage Degradation Parameters on Stress Triaxiality

A Proposal on Ultra-Low Cycle Fatigue Damage Evaluation of Structural Steels

Approach to investigate pre-nucleation fatigue damage of cyclically loaded metals using Vickers microhardness tests

Influence of Inclusion Size on Fatigue Behavior of High Strength Steels in the Gigacycle Fatigue Regime

Dependence of Fatigue Strength on Inclusion Size for High-Strength Steels in Very High Cycle Fatigue Regime

A fatigue life prediction approach to interior cracking induced high cycle and very high cycle fatigue for surface‐carburized steels

Estimation of Maximum Inclusion Size and Fatigue Strength in High-Strength ADF1 Steel

High-Cycle Fatigue Fracture Behavior of Ultrahigh Strength Steels

An Insight into the Creep-Fatigue Damage Localization in Welded Joints Based on Crystal Plasticity Finite Element Method

Influence of Non-Metallic Inclusions on Very High-Cycle Fatigue Performance of High-Strength Steels and Interpretation via Crystal Plasticity Finite Element Method

Sem in Situ Observations to the Effects of Inclusions on Initiation and Propagation of the Low Cyclic Fatigue Crack in Super Strength Steel

Experimental and Numerical Characterization of Low Cycle Fatigue and Creep Fatigue Behaviour of P92 Steel Welded Joint

The Effect of Inclusions on the Fatigue Behavior of Fine-Grained High Strength 42crmovnb Steel

Non-inclusion induced crack initiation in multiphase high-strength steel during very high cycle fatigue

Relationship among Fatigue Life, Inclusion Size and Hydrogen Concentration for High-Strength Steel in the VHCF Regime

Microstructure-Based Fatigue Modeling with Residual Stresses: Effect of Inclusion Shape on Very High Cycle Fatigue Life

Study on Inclusion Induced Fatigue Crack Initiation and Propagation in Ultra-High Strength Steel for Aerospace Application