Abstract:To develop a fast and economical process of preparing NiAl coatings on steel substrates, the plane wave propagating mode of combustion synthesis was employed in this study. Prior to the combustion process, Ni/Al compacts were obtained with a pressure of 180 MPa. To improve the adhesion strength of the NiAl coating, a Cu-Zn foil, which could be melted by the heat in the combustion synthesis process and acted as a joining layer, was mounted between the Ni/Al compact and the Q235 substrate. The combustion reaction of the Ni/Al compact was triggered by an arc, and propagated along the substrate surface. The phase composition and microstructure of the as-synthesized NiAl coating and the joining area were examined by X-ray diffraction (XRD) and scanning electron microscopy (SEM) equipped with energy dispersive spectroscopy. The XRD results showed that the coating was composed of NiAl and some Ni2Al3 when the preheating temperature was lower than 300 degrees C. When the preheating temperature reached this value, only NiAl could be found. Additionally, in the joining area, CU0.64Zn0.36, NiAl, Ni3Al as well as unreacted Ni could be characterized. The influences of the applied pressure and the preheating temperature on the adhesion strength of the as-synthesized coating were also investigated. When the applied pressure was enhanced from 10 to 40 MPa, the shear strength between the NiAl coating and the substrate was increased from 52.3 to 60.8 MPa. However, when the preheating temperature rose from 0 to 300 degrees C, the shear strength increased firstly and then decreased with it. When the preheating temperature was 100 degrees C, the shear strength reached the maximum value, 64.7 MPa.

Study on Microstructure and Properties of Plasma In-situ Synthesis of Ni-Al Intermetallics Coating

Study on Structure and Properties of Plasma Spraying Fe-Ni-B Coating

Study On Tic/Ni Coating By Laser Alloying In-Situ Fabricated In The Internal Surface Of N80 Tubing

Microstructure characterization of AlCoCrFeNiTi high-entropy alloy coating produced by atmospheric plasma spraying

Microstructure, Oxidation Behavior and Adhesion of a CoNiCrAlTaY Coating Deposited on a High Nb–TiAl Alloy by Plasma Surface Metallizing Technique

Microstructure and Corrosion Properties of Plasma Arc Spraying Ni-based Coatings

Study on Microstructure and Properties of FeNiCr/Ni Coated Cr_3C_2 Coatings Deposited by High Velocity Arc Spraying

Study on Microstructure and Properties of Ni- Al2O3 Composite Coating

Microstructure, Mechanical and Tribological Properties of Plasma-Sprayed NiCrAlY-Mo-Ag Coatings from Conventional and Nanostructured Powders

Synthesis, Structure, and Properties of the High Nb–TiAl Alloy after Ni Coatings by Plasma Surface Alloying Technique

Microstructure of NiCoCrAlY component in plasma sprayed ZrO2/NiCoCrAlY graded coating

The Preparation and Properties of Ni2Al3 Intermetallic Compound Coating

Microstructural and tribological characterization of NiAl matrix self-lubricating composite coatings by atmospheric plasma spraying

Study on performance of nano-zirconia coating deposited by plasma spraying

Microstructure and formation mechanism of Ni-Al intermetallic compounds fabricated by reaction synthesis

Microstructure and Adhesion Strength of NiAl Coating Prepared on Q235 Substrate by Combustion Synthesis Assisted with Cu-Zn Interlayer

Microstructure and Properties of Cr-Al2O3 Cermet Coating Obtained by Plasma in Situ Synthesis

Microstructure and tribological behavior of plasma spray Ni60 alloy coating deposited on ZL109 aluminum alloy substrate

Microstructure and properties of plasma clad Ni composite coating

The Microstructure and Deposition Behavior of NiCr Alloy Coatings Using Laminar Plasma Spraying

Microstructure and Properties of NiAl Intermetallics Sintered by the Spark Plasma Sintering