Pitting Corrosion Property of Simulated Welding HAZ in 2205DDS

ZHANG Jian-xun,LI Qing-yan,LI Wei-wei,ZHANG Tian-hong,LIU Ya-xu

DOI: https://doi.org/10.3969/j.issn.1001-4381.2006.08.007

2006-01-01

Abstract:The relationship of the microstructures and pitting corrosion property of simulated welding heat affected zone(HAZ) in 2205 duplex stainless steel was investigated using thermal simulator and pitting corrosion testing.The effects of cooling time on the pitting corrosion property of simulated HAZ were studied at the same time.The results showed that the cooling time had influences on the pitting corrosion property of the simulated HAZ,that the ferrite content decreased and precipitate of carbide and nitride in ferrite increases as increasing cooling time,that pitting corrosion rate and pitting corrosion area ratio were higher in simulated HAZ than in base metal and decreased with the increase of the cooling time,that the maximum pitting corrosion depth was lower in simulated HAZ than that in base metal and increases with the cooling time t_(8/5),and that the pitting corrosion property of the simulated HAZ was the same as base metal when the cooling time was about 100s.