Energy transfer between Ce 3+ and Tb 3+ and the enhanced luminescence of a green phosphor SrB 2 O 4 :Ce 3+ , Tb 3+ , Na +
Shaojun Sun,Li Wu,Huan Yi,Liwei Wu,Jingyuan Ji,Chunling Zhang,Yi Zhang,Yongfa Kong,Jingjun Xu
DOI: https://doi.org/10.1364/OME.6.001172
2016-01-01
Optical Materials Express
Abstract:A series of Ce3+ or Tb3+ doped and Ce3+, Tb3+, and Na+ co-doped SrB2O4 phosphors were synthesized by solid-state reaction method. Luminescence intensity was increased as M+ (M+ = Li+, Na+, K+) ions were used to compensate the valance in SrB2O4:Ce3+, in which the charge compensation by Na+ ion in SrB2O4:Ce3+ showed the strongest luminescence intensity. When the content of Ce3+ was fixed at 2 mol. % by tuning the contents of Tb3+ ions from 1 mol. % to 10 mol. %, SrB2O4:0.02Ce(3+), yTb(3+), zNa(+) showed both an emission (360 nm) from Ce3+ and a yellowish-green emission (541 nm) from Tb3+, which disclose that an effective energy transfer from Ce3+ to Tb3+ exists in the phosphor. The energy transfer efficiency reaches as high as 80.2% for a Tb3+ concentration of 10 mol. %. The QE of SrB2O4:0.02Ce(3+), 0.03Tb(3+), SrB2O4:0.02Ce(3+), 0.03Tb(3+), 0.05Na(+) phosphors are 41.3% and 54.7% excited at 319 nm. The energy transfer mechanism was proved to be dipole-dipole interaction. The CIE chromaticity coordinates of the optimized SrB2O4:0.02Ce(3+), 0.03Tb(3+), 0.05Na(+) phosphor, which were thermal stable revealed by temperature-dependent PL results, were calculated to be (0.3035, 0.4812). (C) 2016 Optical Society of America