Vortex phase diagram and transition in (Bi1.6Pb0.4Sr2Ca2Cu3O10-δ)1-x(SnO2)x superconductors
An T. Pham,Tien Le,Vuong Thi Anh Hong,Hanoh Lee,T. Park,Nguyen Duy Thien,Do Thi Kim Anh,Nguyen Hoang Nam,Nguyen Thanh Binh,Nguyen K. Man,Pham Ngoc Thao,Dang T.B. Hop,T. Miyanaga,Q. Nghi Pham,Duc H. Tran
DOI: https://doi.org/10.1016/j.rinp.2024.107887
IF: 4.565
2024-01-01
Results in Physics
Abstract:The superconducting vortex phase diagram of (Bi1.6Pb0.4Sr2Ca2Cu3O10-δ)1-x(SnO2)x ceramics, where x = 0, 0.002, 0.004, 0.006, 0.008, and 0.010, was investigated using resistivity measurement under magnetic fields. If the value of the offset critical temperature (Tc,offset) monotonously decreased on the SnO2-added samples, then the mean-field critical temperature (Tmf) would slightly improve on the x = 0.002 sample. The excess conductivity of all samples was analyzed based on the Aslamazov–Larkin and Lawrence–Doniach models. The c-axis coherence length at 0 K (ξc(0)) and the interlayer coupling strength were optimized on the x = 0.002 sample. The activation energy (U0) calculated using the Arrhenius model was also increased, and the maximum for the x = 0.002 sample was reached. The upper critical field (Bc2) deduced using the Werthamer–Helfand–Hohenberg model was also enhanced for the x = 0.002 sample. The small bundle field (Bsb), large bundle field (Blb), irreversibility field (Birr), and Bc2 were combined for the vortex phase (B-T) diagram of the x = 0.000 and x = 0.002 samples. All pinning regimes of the x = 0.002 sample were extended, clearly revealing the improvements in the flux pinning properties in that sample.