Abstract:In this paper, We prepared two groups of the glasses, the first group is Ge x As 20 Se 80-x with x from 5 % to 32.5 %, the second group is Ge x Sb 20 Se 80-x with x from 5 % to 25 %, using the conventional melt-quench method, and investigated the effect of the elemental substitution of As by Sb on the threshold behaviors in Ge x As(Sb) 20 Se 80-x glasses. We aimed to understand that,to which degree the topological model and chemical order model can explain the correlation between the physical properties and glass compositions, and how the chemical composition can affect the transition threshold in the glasses. Glass transition temperature was measured by the differential scanning calorimeter (Mettler-Toledo, DSC1) with different scanning rates from 5 K/min to 30 K/min under a uniform nitrogen gas flow of 50 mL/min, the density of the glasses was measured by a Mettler H20 balance with a MgO crystal used as a reference. Samples from each glass composition were weighed five times and the average density was recorded, the refractive index of the glass at 1.5 um was measured by a Metricon Model 2010 prism coupler. Raman spectra were measured from a T64000 Jobin-Yvon-Horiba micro-Raman spectrometer equipped with a liquid-nitrogen-cooled CCD detector. The 830 nm laser line was used as an excitation source, and the laser power was kept as small as possible to avoid any photo-induced effects. The resolution of the spectrometer was about 0.5 cm -1 . The result from systematic measurements of these physical parameters shows that, while the transition thresholds at MCN=2.4 and 2.67 were verified in the Ge-As-Se glasses with ideal covalent network, these two transitions represent the covalent network structure inside the glass from an under-constrained “floppy” network to an over-constrained “rigid” phase and from the two-dimensional to the three-dimensional “stressed rigid” phase respectively. However, when As is substituted by Sb, the Ge x Sb 20 Se 80-x glass with non-ideal covalent network will change of the transition thresholds, which changes to the chemically stoichiometric composition. We further deconvolved Raman scattering spectra into different structural units and the change of their respective intensity showed the same behavior, and this was ascribed to the chemical effect induced by a large difference of the atomic radius between As and Sb, and a relatively strong ionic feature of the element Sb.

Effect of the substitution of S for Se on the structure of the glasses in the system GeSbSSe

Effect of the elemental substitution on threshold behaviours in Ge-As(Sb)-Se glasses

Effects of the Se Substitution for Te on the Structure and Properties of Glasses in the Ag30As28(SexTe100-x)42 System

Correlation Between Acousto-Optic and Structural Properties of Ge–Sb–S Chalcogenide Glasses

Effects of S-doping on the Electronic Transition, Band Gap, and Optical Absorption of GaSe1−xSx Single Crystals

Study of Effects of Te Addition and Oxygen Contamination on the Surface Short Range Order Structure of GeBiSe Glass by XPS

Structure of GeS2-SbSI Glasses by Raman Spectroscopy: Rapid Communications of the American Ceramic Society

Thermal and optical properties of GeS2-based chalcogenide glasses

Intermediate phase, network demixing, boson and floppy modes, and compositional trends in glass transition temperatures of binary AsxS1-x system

Effect of Annealing Conditions on the Physio-Chemical Properties of Spin-Coated As2se3 Chalcogenide Glass Films

Optical properties and structural rigidity of [(GeSe2)75(Sb2Se3)25]100−xTex chalcogenide glasses for potential applications in infrared filters and lenses

Atomic level structure of Ge-Sb-S glasses: chemical short range order and long Sb-S bonds

Investigation of the substitution of mercury by silver in Ag 2 S-HgS-GeS 2 glasses: Macroscopic, electrical and vibrational properties

The Third-Order Optical Nonlinearities of Ge–Ga–Sb(In)–S Chalcogenide Glasses

Effect of tellurium addition on the optical and physical properties of germanium selenide glassy semiconductors

Effect Of Sb2o3 On Thermal Properties Of Glasses In Bi2o3-B2o3-Sio2 System

Structure and Luminescent Properties of Glasses in the GeS2-Ga2S3-Sb2S3:Pr3+ System

Chemical order in Ge-Ga-Sb-Se glasses

Spin–orbit coupling effect on electronic, linear and nonlinear optical properties of Bi2S3 and the ternary bismuth sulfide Bi2S2.75Se0.25: Ab-initio calculations

Thermal and Optical Properties of the Ga–Ge–Sb–Se Glasses

Structural evolution of Ge–Ga–Se glass upon compositional change across the stoichiometric GeSe2–Ga2Se3 tie-line