Abstract:RE/TiO2 photocatalysts were prepared by the sol–gel method using rare earth (RE=La3+, Ce3+, Er3+, Pr3+, Gd3+, Nd3+, Sm3+) metal salts and tetra-n-butyl titanate as precursors, and were characterized by XRD, IR, UV–vis diffuse reflection, and transient absorption spectra. Their photocatalytic activities were evaluated using nitrite as a decomposition objective. As a result, suitable content of doping rare earth in TiO2 can efficiently extend the light absorption properties to the visible region. At the same time, it is beneficial to NO2− adsorption over the catalysts due to rare earth doping. RE/TiO2 samples can enhance the photocatalytic activity to some extent as compared with naked TiO2. The increase in photoactivity is probably due to the higher adsorption, red shifts to a longer wavelength, and the increase in the interfacial electron transfer rate. Nitrite is almost completely degraded over RE/TiO2 catalysts after longer irradiation, which is different from Degussa P-25 with a plateau of activity after ca. 20 min irradiation. Gd3+-doped TiO2 showed the highest reaction activity among all concerned RE-doped samples because of its specific characteristics. The amount of RE doping was an important factor affecting photocatalytic activity; the optimum amount of RE doping is ca. 0.5 wt%, at which each RE/TiO2 sample shows the most reactivity. The photocatalytic degradation reaction of nitrite over Gd3+-doped samples and P-25 follows apparent first order kinetics, which is different from that of Sm3+, Ce3+, Er3+, Pr3+, La3+, and Nd3+-doped TiO2 catalysts, which obey zero-order kinetics, indicating that these processes were dominated by electron–hole recombination.

Photocatalytic Activity of Nd and Pr Co-doped TiO_2

Surface Properties and Photocatalytic Activity of Pr~(3+)-Doped TiO_2 Nano-Powders

STUDY ON THE PHOTOCATALYTIC PROPERTY OF NANO Nd-TiO_2

(Mo+n) Codoped TiO2 for Enhanced Visible-Light Photoactivity

Mechanisms of Enhancement Photocatalytic Properties and Activity Nd3+-Doped Tio2 for Methyl Orange Degradation

Preparation and Photocatalytic Properties of Mo-doped TiO2

A hydrothermal synthesis of Pr3+ doped mesoporous TiO2 for UV light photocatalysis.

Preparation,characterization and Photo Activities of TiO2/Pr2O3 Nano-Powders

Synthesis and Photocatalytic Activity of Sulfate Modified Nd-doped TiO2 under Visible Light Irradiation

Effects of Rare Earth Elements and Nitrogen Co‐Doped on the Photocatalytic Performance of TiO2

Effects of Nd-doping on crystal phase, structure and photocatalytic performance of TiO 2 powders prepared by sol-gel method

Study on photodegradation of methyl orange using co-doped TiO2 with Y3+ and N

Preparation And Photo-Catalytic Activity Of Tm Doped Tio2 Nanoparticles

Photocatalytic Properties of Nd and C Codoped TiO2 with the Whole Range of Visible Light Absorption

Study on Preparation and Photo Catalytic Activity of Nano TiO_2 with Nd~(3+)、Eu~(3+)、Tb~(3+) Doping

The Preparation, Characterization, and Their Photocatalytic Activities of Rare-Earth-Doped TiO2 Nanoparticles

The effect of neodymium ion doping on the photocatalytic properties of nano-titanium dioxide

Characterization and Mechanism Analysis of Mo–N-co-doped TiO2 Nano-Photocatalyst and Its Enhanced Visible Activity

Preparation of Highly Visible-Light Active N-doped TiO2 Photocatalyst

Preparation,Charaterization,and Photocatalytic Activity of TiO2/Mo-TiO2

Enhanced photocatalytic activities of Nd-doped TiO2 under visible light using a facile sol-gel method