Abstract:For the assessment of the influence of corrosion on behavior of residential steel structures, firstly, indoor salt spray accelerated corrosion tests of Q235B steel with and without coating respectively were carried out for 6 400 hours at most, which resulted in the corrosion depth equal to 50-year corrosion in Shanghai according to existing record. Secondly, mechanical property of these steel was tested. Thirdly, indoor salt spray accelerated corrosion tests on two groups of welded H-section beams with and without coating respectively were performed for 2 400 hours at most, which resulted in the corrosion depth equal to 20-year corrosion in Shanghai according to existing record. Finally, static load bearing capacity of these beams was examined. The relationships of yielding strength, tensile strength and elongation respectively with mass loss rate for steel subjected to corrosion were given using the method of least squares. The current investigation indicates that for the H-section beams with coating subjected to 2 400-hour corrosion, their load bearing capacities decrease significantly, and the corresponding deflections increase obviously. It is found that the plate thickness is an important factor influencing the behavior of H-section beams subjected to corrosion after a comparison between the two geometrical parameters of plate thickness and the surface area per length. The thinner the thickness of a flange or a web is, the more load carrying capacity decreases and the more deflection increases.

Experimental Study on Influence of Corrosion on Behavior of Steel Material and Steel Beams