Abstract:Titanium alloys are known for being difficult to machine. Within the groups of Ti alloys, the machinability is reduced when going from the α-alloys, to α + β, and finally to near-β or β-alloys. Uncoated cemented carbide is traditionally used for machining these alloys and finding a suitable coating to improve the performance is a challenge due to the high strength of Ti alloys and the high chemical reactivity of Ti with tool and coating materials at the temperatures achieved during cutting. The PVD applied Ti x Al 1-x N (x = 0.4–0.7) is generally recommended for machining Ti alloys and a top layer of NbN has shown promising performance in milling applications. This study systematically explores the wear mechanisms of either uncoated WC-12%Co or its Ti 0.45 Al 0.55 N-NbN coated version in the milling of Ti alloys ranging from near-α (Ti-6Al-2Sn-4Zr-2Mo), α + β (Ti-6Al-2Sn-4Zr-6Mo), and near-β (Ti-5Al-5Mo-5 V-3Cr) alloys. The wear evolution is explored by studying as-worn tools and their cross-section using SEM-XEDS and EBSD after having reached 10%, 30%, 50%, and 100% of the full tool life at a flank wear criterion VB = 200 μm. The coating is removed within seconds of engagement and fails by cracking within the bulk and PVD droplet defects can initiate such cracks. Diffusional dissolution of the coating may be active on a minor scale, but the rapid mechanical failure shows the need for a more robust coating formulation. Exposed cemented carbide is worn at varying intensities when machining the Ti alloys. The highest wear rate is achieved in milling α + β Ti-6246, followed by a moderate wear rate in near-β Ti-5553, and with a slower wear rate in milling near-α Ti-6242 which is explained varying intensities in oxidation wear, diffusional dissolution, and mechanical cracking. Diffusional loss of C gives rounder WC grains and remaining W at the interface is removed by the chip flow. Diffusional loss of Co gives reduced grain bonding and loss of the dampening effect that leads to fractures in WC grains. Specifically in milling α + β Ti-6246 and in minor scale in near-α Ti-6242, there is formation of CoWO 4 ceramic present several μm into the tool and its formation is facilitated by the oxidation of binder with resolved W. Fractures within the CoWO 4 explains the high wear rate. Cracks also propagate in binder regions initiated from weakened interface regions due to diffusional loss of C and Co.

Wear of Tool with TiA1N Coating in High-speed Milling of Particle Reinforced Aluminum Matrix Composites

Application of Magnetron Sputter Ion Plated CrAlTiN Composite Coating in Improving Wear Resistance of Milling Cutter

Effect of Al Content on the Wear Evolution of Ti1-xAlxN-Coated Tools Milling Ti-6Al-4V Alloy

Analysis of tool wear of TiAlN coated tool, machined surface morphology and chip during titanium alloy milling

Wear of End Mills with Carbon Coatings When Aluminum Alloy A97075 High-Speed Processing

Study on the Orthogonal Cutting Process of Al7050T7451 with Uncoated and Coated Tools

Wear Behavior of SiAlON Ceramic Tool and Its Effects During High-Speed Cutting

Study on tool wear of cemented carbide coated tool in milling of SiCp/Al composites

Finite element analysis of Ti 1-x Al x N coated tools cutting performance and tool wear during Ti-6Al-4V milling

An investigation of the wear mechanism for carbide tools in face milling the Ti-5Al-4.75Mo-4.75V-1Cr-1Fe alloy

Wear characteristics and performance in side milling of Ti 2 AlNb intermetallic alloys with coated and uncoated end mills

Experimental Investigation on Tool Wear Characteristics of PVD and CVD Coatings During Face Milling of Ti6242S and Ti-555 Titanium Alloys

Effects of tool coating and tool wear on the surface and chip morphology in side milling of Ti2AlNb intermetallic alloys

The Evaluation of Tool Wears in Machining of Sicp/Al Composites

Enhancing Tool Performance in High-Speed End Milling of Ti-6Al-4V Alloy: The Role of AlCrN PVD Coatings and Resistance to Chipping Wear

On the wear mechanisms of uncoated and coated carbide tools in milling titanium alloys

Analysis of Tool Wear in GH4169 Material Milling Process

Wear Mechanism of High-Speed Turning Ti-6Al-4V with TiAlN and AlTiN Coated Tools in Dry and MQL Conditions

Evaluation of the performance of coated carbide tools in face milling TC6 alloy under dry condition

Analysis of tool wear and cutting characteristics in milling of powder metallurgy nickel-based superalloy by various coatings

Study on Coated Tool Wear in High-Speed MQL Machining of TC4 Titanium Alloy