Abstract:This paper reports the synthesis of semiconductor nanocrystals of PbS through a facile and inexpensive synthetic route between lead acetate [Pb(Ac)2·3H2O] and dithioglycol (HSCH2CH2SH) without any surfactant. The products were characterized by x-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution TEM (HRTEM), Raman spectroscopy, x-ray photelectron spectroscopy (XPS) and infrared (IR) spectroscopy. The size of cube-shaped PbS nanocrystals can be controlled by changing the relative amount of Pb(Ac)2·3H2O and dithioglycol. Smaller cube-shaped PbS nanocrystals were obtained at higher sulfur content in the reaction system. The nanometre-sized single crystals of PbS measure ~83 nm × 59 nm × 22 nm and 39 nm × 10 nm × 7 nm, for lead acetate:dithioglycol ratios of 1:0.375 (denoted as PbS-1) and 1:1.5 (denoted as PbS-2), respectively, when a mixture of NaOH solution of lead acetate and ethyl alcohol solution of dithioglycol is maintained at 220 °C for 4 h in a Teflon-lined autoclave. XRD patterns and HRTEM images confirm the crystalline structure of the PbS crystals. TEM helped to determine the dimension of the single crystals. Raman, XPS and IR helped to further demonstrate the purity of the as-synthesized samples. The optical absorption spectra of suspensions of the these crystals in glycol show shifts in absorption band edge for as-prepared sample PbS-1 from 246 to 271 nm and for PbS-2 from 246 to 275 nm, after four days of storage, respectively. The photoluminescence peaks from the two samples are located at 434 and 433 nm for photoexcitation radiation of 315–355 nm, thus exhibiting a Stokes shift compared with band edge energy. The principal contribution of this work is that the nanometre-size PbS single crystals are prepared without using a surfactant or templating agent. The formation of a five-membered ring via the chelation between the Pb2+ ion and dithioglycol is considered to be crucial in this mechanism.

Pbs Nanocrystals Embedded in Microstructures Produced by Micromoulding in Capillaries

Preparation of Pbs/Poly(Acrylic Acid) Nanocrystal Micropatterns by Soft Lithography

The Preparation And Characterization Of Zns/Pmma Nanocomposites

Development of Structure-tailored and Composite Magnetic-Fluorescent Microspheres Through the PRI Method

Morphology Control of Pbs Nanocrystals by A Novel Hydrothermal Process

A Novel Hydrothermal Synthesis of Single Crystalline Pbs Nanorods and Their Characterization

Shape-Controlled Syntheses of Pbs Submicro-/Nano-Crystals Via Hydrothermal Method

A novel aqueous-phase route to prepare flower-shaped PbS micron crystals

PbS/epoxy resin nanocomposite prepared by a novel method

Synthesis of Pbs Nanoparticles in Polymer Matrices

Synthesis and Characterization of Pbs Nanocrystals in Water/C12e9/Cyclohexane Microemulsions

Synthesis and Characterization of PbS Nanocrystallites in Random Copolymer Ionomers

Facile Biomolecule-assisted Synthesis of PbS Nanostructures with Various Morphologies

A New Approach to the Synthesis of Nanocrystal Conjugated Polymer Composites

A room temperature chemical route to nanocrystalline PbS semiconductor

Hydrothermal Synthesis and Characterization of Lead Chromate 1d Nanostructures and Pbcr4o13/Pbs Nanocomposites

Synthesis Of Lead Sulfide/(Polyvinyl Acetate) Nanocomposites With Controllable Morphology

Growth and photoluminescence properties of PbS nanocubes

Controlled Synthesis of Semiconductor PbS Nanocrystals and Nanowires Inside Mesoporous Silica SBA-15 Phase

L-Cysteine-Assisted Synthesis of PbS Nanocube-Based Pagoda-like Hierarchical Architectures

Controllable synthesis, characterization and optical properties of colloidal PbS/gelatin core-shell nanocrystals