Progressive failure analysis on composite π joint

CHEN Shenyan,LIN Zhiwei,HUANG Hai,LIANG Xianzhu
DOI: https://doi.org/10.3969/j.issn.1006-0871.2011.03.005
2011-01-01
Abstract:As to the complex failure modes of composite π joint,the progressive failure procedure of a structure is simulated by material stiffness degradation method.The 3D finite element model of a composite π joint is established by Abaqus;five failure modes of composite laminates are differentiated by using 3D Hashin failure criteria and Ye-delamination criterion,an elastic-perfectly plastic material model is applied to adhesive material to simulate the adhesive failure,and a progressive failure analysis subroutine considering both the composite laminates and adhesive failures is developed in Abaqus,in which six field variables are defined to represent different failure modes: fiber tensile failure,fiber buckling,matrix tensile cracking,matrix compression cracking,delamination failure and adhesive failure.The failure analysis is performed on the model under given increasing tensile loads,and the results show that the method is effective in predicting initial failure position,initial failure load and final failure load for composite π joint.
What problem does this paper attempt to address?