Regioselective Synthesis of Mononitrochlorobenzene with Nanosolid Acid Catalyst

XI Li-min,Yang Yi-wen
2006-01-01
Chinese Journal of Energetic Materials
Abstract:The new nanosolid superacid Fe_2O_3/(SO_4)~(2-) was prepared by using nanometer chemical technology.Samples were characterized by XRD and TEM.The results show that Fe_2O_3/(SO_4)~(2-) is superfine solid belonging to nanocrystal and its average size is(40 nm) with good distribution.The regioselection and activity of chlorobenzene nitration was raised,when the nanosolid superacid(Fe_2O_3/(SO_4)~(2-)) was taken as the catalyst.The optimum reaction conditions were found out.Thus activated temperature of catalyst was 600 ℃,the reaction was carried out at 50 ℃ for 6 h with n(nitric acid)/n(chlorobenzene) equalling to 3.5 and m(chlorobenzene)/m(catalyst) equalling to 20 to get the yield of 78.7%,the ratio between para-and ortho-mononitrochlorobenzene(P/O) reaching up to 4.8.