Abstract:Bismuth sodium titanate Bi_(0.5)Na_(0.5)TiO_3(BNT)manometer powders are prepared by Pechini method.The sintered BNT ceramics possess excellent piezoelectric properties with the d_(33) value as high as 105 pC/N,which is the highest value reported till now.The well-saturated P-E hysteresis loop can be obtained at a drive field of 80 kV/cm.The remanent polarization P_r and coercive field E_c are 37 μC/cm~2 and 61.2 kV/cm respectively.Moreover,the BNT ceramics can be fully polarized under 40 kV/cm DC electric field at a temperature of 60 ℃.The results show that appropriate Bi~(3+) content is helpful to obtain dense,fine grain microstructure and better ferroelectric and piezoelectric properties.

Study on the Bi0.5Na0.5TiO3 Ceramics Prepared by Pechini Method