Effect of aging on electrochemical corrosion behavior of 2205 stainless steel in simulated formation water

SHI Shu-kun,WANG Jun,LI Hai-feng,WANG Yuan-sheng,YAN Jing,FAN Hong-yuan
DOI: https://doi.org/10.13289/j.issn.1009-6264.2012.01.013
2012-01-01
Abstract:Electrochemical behavior of 2205 stainless steel in simulated formation water saturated with CO2 at 85 ℃ were studied by potentio-dynamic polarization method and electrochemical impendence spectroscopy(EIS).Microstructure of the alloy was observed by metallurgical microscopy,X-ray diffraction(XRD),scanning electron microscopy(SEM and EDS).The results show that when aged from 800 ℃ to 900 ℃,self-corrosion potential of the duplex stainless steel increases as the aging temperature increases and the current density first increases and then decreases.Besides,as the aging time increases at the same aged temperature,self-corrosion potential increases and passive region is gradually reduced until it disappears,so the corrosion rate increases with time.Microscopic analysis indicates that the main reason for the deterioration of corrosion resistance of the duplex stainless steel aged from 800 ℃ to 900 ℃ is the precipitation of σ phase.
What problem does this paper attempt to address?