Effects of Rare Earth Element Cerium on the Microstructure and Properties of Hot-dip Aluminum Coatings on 45 Steel

YANG He-mei,LU Qin,ZHANG Jing
DOI: https://doi.org/10.14136/j.cnki.issn1673-2812.2010.05.024
2010-01-01
Abstract:The influences of element cerium on the microstructure and properties of hot-dip aluminum(HDA) coatings on 45 steel were studied by scanning electron microscopy(SEM) and X-ray diffractometry(XRD).The high-temperature oxidation resistance and wear properties of HDA coatings were also evaluated by oxidation weight increase method and using the MM-2000 wear tester,respectively.The results show that grains of HDA coatings are refined and the layer thickness becomes thinner when Ce content is between 0.1 wt.% and 0.25 wt.%.At the same time,the alloy layer of HDA coatings treated by annealing becomes thicker.Ce could restrain the growth of Fe_2Al_5 in the alloy layer.As a result,the alloy layer of HDA coatings consists of FeAl_3 and a little Fe_2Al_5,but the annealed alloy layer consists of FeAl and Fe_3Al.The high-temperature oxidation resistance of HDA coatings and the wear resistance of the annealed alloy layer under oil lubrication are the best when Ce content is 0.25 wt.%.
What problem does this paper attempt to address?