Structural, Thermal, and Optical Properties of GeO2-La2O3-TiO2 Glasses
Wan Jiabao,Zhang Minghui,Su Huaiyu,Cao Zhijun,Liu Xuechao,Xie Jiansheng,Wang Xiangyuan,Shi Yinghui,Wang Liang,Lei Shuijin
DOI: https://doi.org/10.15541/jim20230068
IF: 1.292
2023-01-01
Journal of Inorganic Materials
Abstract:La2O3-TiO2 glasses show promising application prospect in fields of lenses, optical windows, and optical communication, owing to their high refractive index and excellent performance. However, this glass cannot be prepared into large size because of its weak glass forming ability, which seriously limits its application. In this study, introducing the network former GeO2 can effectively improve the glass forming ability, so that large-sized GeO2-La2O3-TiO2 (GLT) glass can be prepared using conventional methods. Differential thermal analysis shows that GLT glasses have high glass transition temperature (T-g) and strong resistance to precipitation, with Tg and Delta T (Tc-onset-T-g) greater than 833 and 209 degrees C, respectively. The refractive index is up to 2.06. The transmittance can reach 78% in the visible and near-infrared wavelength bands. The glass forming ability and thermal stability can be weakened by increasing the content of TiO2. The molar volume and oxygen electron polarizability exhibit the same variation trends as the refractive index of the samples. This result is important for developing new devices with high performance, light weight, and small size.