Properties Improvement of Egg Albumen by Conjugation with CMC or CMC-Na

Bao-li XU,Bin LI,Bo ZHU,Ying XIA,Jin-song FAN,Xiao-dong ZHENG,Jie CAI,Mei-hu MA

DOI: https://doi.org/10.7506/spkx1002-6630-201103011

2011-01-01

Abstract:Egg white was blended with sodium carboxymethyl cellulose(CMC-Na) or carboxymethyl cellulose(CMC) of certain concentration respectively,and the dry-heated products were obtained at relative humidity(75%) after freeze drying. The products were analyzed on gel strength,color scale,scanning electron microscope observation,SDS-PAGE,and Differential Scanning Calorimetric(DSC) at intervals. The results showed that a significant increase in the gel strength of egg white,more uniform and compact gel network structure and a significant reduction in the content of proteins with small molecular weight were found after 2 days of reaction at 60 ℃. The foaming capacity of egg albumen was found to be enhanced significantly by 2-day-long reaction,but the excessive cross-linking might lead to a large molecular weight,decrease the solubility of egg white powder and darken its color. Adding CMC or CMC-Na at a concentration of 0.25% resulted in the best foaming capacity at 60 ℃,with 0.6-fold and 0.5-fold increases in comparison with a blank sample,respectively and meanwhile,a significant improvement was observed for foam stability. It was proved that a novel egg white powder with both higher gel property and foaming capacity can be obtained under the reaction conditions.