Biomechanical evaluation of augmentation of osteoporotic cancellous bone with injectable nano-hydroxyapatite/polyamide cement
Wei Huang,Hong An,Dian-ming Jiang,Yu-bao Li,Jie Wei,Ting-wu Qin
DOI: https://doi.org/10.3321/j.issn:1673-8225.2006.01.020
2006-01-01
Abstract:AIM: To investigate the in vitro biomechanical performance of new injectable nano-hydroxyapatite n-HA/ polyamide 66 composite cements different in n-HA content in the augmentation of osteoporotic cancellous bone to choose suitable bone cement for the clinical applicability. METHODS: This experiment was performed in Chongqing University of Medical Sciences, Research Center For Nano-Biomaterials of Sichuan University and State Key Laboratory of Biotherapy of Sichuan University from January 2001 to January 2003. The cadaveric T1-T6 thoracic vertebrae and bilateral femur samples of five elderly people and one young people were obtained and were showed no pathologic lesion and damage by roentgenography. In axial compressive testing, the 34 vertebral bodies resected the disc and posterior parts were used. ①The 28 elderly vertebral bodies were randomly divided into four groups, 60% n-HA/PA66 composite cement HP1 group, 70% n-HA/PA66 composite cement HP2 group, 80% n-HA/PA66 composite cement HP3 group and osteoporosis group, respectively with 7 specimens in each group. The 6 young vertebral bodies were used as normal control group. ②Vertebroplasty was performed with 5 mL 60%, 70% and 80% n-HA/PA66 composite cements in HP1,HP2 and HP3 groups, respectively. Those in the osteoporosis and normal control groups were only punctured. ③The loading-displacement and pressure-displacement data of every sample were measured, and sampling frequency was 10 Hz. In the torsional testing, the cancellous bone of 10 femoral condyles was used. ①Randomly, 8 elderly femoral condyles were divided into 4 groups: HP1, HP2, HP3 groups and osteoporosis group, 2 condyles in every group the 2 young femoral condyles were regarded as normal control group. ②Those in the HP1,HP2 and HP3 groups were injected compressively with 20 mL 60%, 70% and 80% n-HA/PA66 cement, respectively. Those in the osteoporosis and normal control groups were only punctured. The cancellous bones of condyles were cut into about 10 mm×10 mm×30 mm bars in size, 5 bars in every group. Torsional strength and stiffness were measured.RESULTS: All data of 34 vertebral bodies in compressive testing and 10 femoral condyles in torsional testing were involved in the result analysis. In compressive testing, ①Determination of yield strength and ultimate compressive strength in every group: The yield strength and ultimate compressive strength in the HP1,HP2 and HP3 groups increased markedly than that in osteoporosis group, especially in the HP1 and HP2 groups P < 0.05. But these parameters in cement-injected groups were obviously lower than that in normal group P < 0.05. ②Determination of compressive stiffness of every group: The compressive stiffness in HP1,HP2 and HP3 groups increased markedly than that in the osteoporosis group, especially in the HP1 and HP2 groups P < 0.05, but this parameter in cement-injected groups were lower than that in the normal control group, especially in the HP3 group P < 0.05. In torsional testing, ①Determination of torsional strength of every group: The torsional strength in the HP1,HP2 and HP3 groups increased markedly than that in the osteoporosis group, especially in the HP1 and HP2 groups P < 0.05, but the parameter in cement-injected groups were obviously lower than that in normal control group, especially in the HP2 and HP3 groups P < 0.05. ②Determination of the compressive stiffness of every group: That in the HP1,HP2 and HP3 groups increased markedly than that in the osteoporosis group, especially in the HP1 and HP2 group P < 0.05, but this parameter in cement-injected groups was obviously lower than that in the normal control group, especially in the HP3 group P < 0.05 CONCLUSION: The injectable n-HA/PA66 composite cement is capable to strengthen the compressive strength and the torsional strength of osteoporotic cancellous bone, treat osteoporotic fracture and prevent the occurrence of centrum fracture. The 60% and 70% cement has better compressive strength and the torsional strength, and more accords with the requirement of clinical application.