Adsorption Dynamics and Distribution Characteristics of Humic Acid on Surface of Biotite
LI Jifu,ZHANG Wenjun,LI Xiaokun,ZHU Jianqiang,LU Jianwei
DOI: https://doi.org/10.11766/trxb201605190254
2016-01-01
Abstract:Objective]An in-situ atomic force microscopy(ScanAsyst)was used to study adsorption dynamic and morphological variation of humic acid on the surface of K-bearing biotite.[Method]Humic acid is a principal component of humic substances,which are the major organic constituents of soil,peat, coal,eutrophied lakes,and ocean water. Humic acid solutions,the same in pH(6.0),but different in concentration(0 mg L-1,100 mg L-1 and 1 000 mg L-1)were prepared out of dried humic acid solid. The mineral sheet used in the in-situ observation was biotite,a kind of phyllosilicate mineral belonging in the mica group(2∶1 type structure),commonly found in soil. The chemical formula of biotite is K (Mg2.46Fe0.45Ti0.09)[AlSi3O10](OH)2. In order to observe how humic acid is adsorbed onto biotite and changed temporally in structure,an experiment was carried out treating the biotite sheet with slightly acidic humic acid solutions,6.0 in pH.[Result] Results show that time was an important factor affecting morphological structure of humic acid on the surface of the sheet. Under the effect of the humic acid solution, 6.0 in pH,the interaction between humic acid molecules and the surface of biotite(001)was dominated with adsorption and and accompanied with some desorption phenomena. The humic acid adsorbed on the surface of the biotite(001)sheet appeared to be in the shape of bulbs,which were congeries of a single or several humic acid molecules,varying in the range of about 1 ~ 5 nm in height within the first 180 min after the treatment;humic acid bulbs remained in dominancy,being about 3 ~ 5 nm in height,or 4 nm on average, during the following period till 300 min,while,sheets of humic acid congeries were found on benches and edges of the biotite sheet and chains of humic aid congeries,too,along the linear edges of the biotite(001) sheet,about 6 ~ 8 nm in height,or 2.5 nm higher than the humic acid bulbs. In addition,humic acid molecules were not just adsorbed or desorbed on the surface of the biotite(001)sheet,and they could also disintegrate the surface structure of the biotite,thus promoting the release of K trapped in the interlayers and Al and Si in the structural lattices.[Conclusion] Therefore,it could be concluded that the reaction in the interface between humic acid and biotite is a process of dissolution-adsorption-aggregation accompanied with desorption and ion release.