SELF ‐ HEALING OF ENGINEERED CEMENTATIONS COMPOSITES ( ECC ) IN CONCRETE REPAIR SYSTEM
K. Chandra,B. Rao,M. Narasaiah
Abstract:Since the concept of high performance concrete was raised in the late 1980’s, it is well known that concrete properties have been greatly improved. However, a larger number of existing concrete structures are suffering deterioration resulting from external or internal causes even during the early stage of service life. Durable repair of concrete has thus drawn more attention. To this end, the main objective of this research is to develop and test a novel method for promoting the self‐healing behavior in concrete repair system. A new type high performance fiber reinforced cementations composites called Engineered Cementations Composites (ECC) has been developed in recent years, characterized by high ductility and improved durability due to the multiple micro‐cracking behavior. In this study, it was proposed that the original ECC with local waste materials was embedded with capsules to investigate the self‐healing potential of this modified ECC material. To realize this self‐healing concept, Super Absorbent Polymers (SAP) can be used as the water reservoir enclosed in the capsules, and then provide available water for self‐healing process when the capsules are ruptured by cracking. Based on this idea, the preliminary experiments, concerning sealing materials and encapsulation procedure, were first carried out. Three ECC mixtures focusing on the influence of capsule content and capsule size were involved. In order to induce artificial cracks, three‐point bending tests have been used to preloaded ECC specimens to different deflection levels. After healing for 28 days, the specimens have been tested again in the three‐point set‐up. The experimental results reveal that the recovered deflection capacity of damaged modified ECC specimens can arrive at 65%‐95% of control specimens, which is higher than that of specimens without capsule. While the recovery of flexural strength and stiffness rarely show improvement. Compared to the case of coarse capsules, the specimens with fine capsules show more reasonable performance on mechanical properties including the deflection capacity, the flexural strength and stiffness as well as their recoveries. The nano‐CT investigation confirmed that moisture transportation took place in more than half of capsules. Under EDX observation, the relatively high concentration of calcium on the crack surface could be considered that the healing product was probably presented in terms of hydration product such as calcium hydroxide or calcium silicate hydrate. However no apparent healed crack was found under ESEM investigation, thus it could be inferred that the healing efficiency was not remarkable in this study. For further research, it is suggested to investigate the contribution of the optimal capsule size and the sufficient water supplement to more effective self‐healing behavior. NAGESWARA RAO B, et al, International Journal of Research Sciences and Advanced Engineering [IJRSAE] Volume 2, Issue 17, PP: 58 67, JAN MAR’ 2017. International Journal of Research Sciences and Advanced Engineering Vol.2 (17), ISSN: 2319-6106, JAN MAR’ 2017. PP: 58 67 INTRODUCTION
Materials Science,Engineering