Nb2O5 Nanobelts: A Lithium Intercalation Host with Large Capacity and High Rate Capability

Mingdeng Wei,Kemei Wei,Masaki Ichihara,Haoshen Zhou

DOI: https://doi.org/10.1016/j.elecom.2008.04.031

IF: 5.443

2008-01-01

Electrochemistry Communications

Abstract:In this study, Nb2O5 nanobelts, with a ca. ∼15nm in thickness, ca. ∼60nm in width and several tens of mircrometers in length, have first been used as the electrode material for lithium intercalation over the potential window of 3.0–1.2V (vs. Li+/Li). It delivers an initial intercalation capacity of 250mAhg−1 at 0.1Ag−1 current density, corresponding to x=2.5 for LxNb2O5, and can still keep relative stable and reaches as large as 180mAhg−1 after 50 cycles. Surprisingly, the electrodes composed of Nb2O5 nanobelts can work smoothly even at high current density of 10Ag−1, and shows higher specific capacity and excellent cycling stable, as well as sloped feature in voltage profile. Cycling test indicates Nb2O5 nanobelts electrode shows a high reversible charge/discharge capacity, high rate capability with excellent cycling stability.