Abstract:1. Srx(Zr0.9Y0.05Yb0.05)O1.95+x‐NiCoCrAlY thermal barrier coatings (TBCs) [SZYY‐1, x = 1.0; SZYY‐2, x = 0.9; SZYY‐3, x = 0.8] were deposited by suspension plasma spraying (SPS) using the corresponding precursors suspension prepared by co‐precipitation. 2. SPS‐SZYY‐2 with columnar crystal structure was found to have the highest number of 1121°C‐1 h high‐temperature thermal cycling, up to 345 times. 3. The effects of microstructure and phase composition on thermal cycling failure of the coating at high temperatures were studied in detail. A finite element model was also proposed to evaluate the thermal stress thermally grown oxide (TGO) morphology of a real coating at different thermal cycling stages. The thermal barrier coatings (TBCs) consisting of Srx(Zr0.9Y0.05Yb0.05)O1.95+x were prepared using the suspension plasma spraying (SPS) method. Precursor suspensions were prepared via co‐precipitation for this purpose. Detailed microstructural, phase composition, and phase content analyses were conducted on these coatings, designated as SZYY‐1 (x = 1.0), SZYY‐2 (x = 0.9), and SZYY‐3 (x = 0.8). Additionally, the coatings underwent a thermal cycling test at 1121°C for 1 h. To assess the morphology of thermally grown oxide (TGO) in a real coating, a finite element model was employed. SPS‐SZYY‐2 with columnar crystal structure was found to have the highest number of thermal cycling, up to 345 times. The thermophysical high‐temperature properties of the coating can be effectively improved through suitable second‐phase content. Microstructural and finite element analyses revealed that stress, primarily caused by the continuous growth of the Co3O4, NiO and Spinel (CNS) layer within TGO, was the predominant factor leading to coating failure. At elevated temperatures, transverse cracks formed at the interface between the bond coating and ceramic top coating due to mismatched thermal expansion and sintering effects, ultimately leading to coating degradation. Therefore, reducing the generation rate of large stresses in the coating, especially shear stresses, can effectively prevent the generation and propagation of transverse cracks and increase the thermal cycling life of TBCs.

Degradation Analysis of YSZ Thermal Barrier Coatings

High Temperature Mechanical Properties of Zirconia Metastable T '-Phase Degraded Yttria Stabilized Zirconia

Phase Transformation Behavior in Air Plasma Sprayed Yttria Stabilized Zirconia Coating

The effect of hydrothermal corrosion on the phase stability, microstructure and thermal cycling behavior of n-YSZ coating

Effect of Sc2O3 Doping on YSZ TBCs: Morphologies, Phase Composition, Mechanical Properties, and High-Temperature Oxidation Resistance

Effect of thermal treatment at high temperature on phase stability and transformation of Yb2O3 and Y2O3 co-doped ZrO2 ceramics

Mechanical Properties Durability of Sc2O3-Y2O3 Co-Stabilized ZrO2 Thermal Barrier Materials for High Temperature Application

Thickness-related failure behaviors of the thermal barrier coatings under thermal gradient cycling

Microstructural and columnar growth characteristics of 7YSZ thermal barrier coatings fabricated by plasma spray physical vapor deposition

EBSD analysis of microstructure changes in YSZ coatings during thermal cycling

On the oxygen vacancy annealing in air plasma sprayed YSZ thermal barrier coatings

Degradation mechanism of dual-phase thermal barrier coatings Gd2Zr2O7 + 8YSZ under hot corrosion in pure Na2SO4

Microstructure Evolution and Impedance Analysis of 7YSZ Thermal Barrier Coating During Gas Thermal-Shock

Thermal Stability of Plasma-Sprayed Thick Thermal Barrier Coatings Using Triplex ProTM-200 Torch

Interface failure behavior of YSZ thermal barrier coatings during thermal shock

Study on Thermal Shock Resistance of Sc2O3 and Y2O3 Co-Stabilized ZrO2 Thermal Barrier Coatings

GdYbZrO thermal barrier coatings by EB-PVD: Phase, microstructure, thermal properties and failure

Residual stress evolution of 8YSZ:Eu coating during thermal cycling studied by Eu3+ photoluminescence piezo-spectroscopy

Investigation of microstructure changes in Al2O3-YSZ coatings and YSZ coatings and their effect on thermal cycle life

Thermal Cycling Behavior and Failure Mechanism of LaTi2Al9O19/YSZ Thermal Barrier Coatings Exposed to Gas Flame

Thermal cycling behavior of Srx(Zr0.9Y0.05Yb0.05)O1.95+x thermal barrier coatings by suspension plasma spraying