Structure and Thermal Shock Resistance of PEO Ceramic Coatings on Ti Alloy

姚忠平,徐用军,贾方舟,王云龙,姜兆华

DOI: https://doi.org/10.3321/j.issn:1002-185X.2009.z2.156

2009-01-01

Rare Metal Materials and Engineering

Abstract:Ceramic coatings were prepared in silicate solution on TC4 alloy by analogous triangle-shape plasma electrolytic oxidation power source. The composition and structure of the coatings were studied by XRD, SEM and EDS, respectively. The thermal shock resistance was examined by thermal shock tests. The results showed that the coating was composed of rutile and anatase TiO(2). Increasing the reaction time, the thickness of the coating increases and the number of micro holes deoreases, whose pore size increases. The results of EDS showed that the content of Si in the coating increases with the reaction time whereas the content variation of Ti showed the opposite trend. At the thermal shock tests of 900 similar to 20 degrees C, the thermal shock resistance of the coating was improved with the reaction time and reached optimum value when the reaction time was 25 min, then decreased with the further extending time. During thermal shock tests the content of the cyrstlized TiO(2) in the coating increases and meantime the micro cracks was found on the coating surface after the thermal shock tests.