Mechanical and Flame Retardant Insulation Properties of Radiation-Crosslinked on Intumescent Flame Retardants/poe Intumescent Flame Retardant Material
LI Jiwei,CHEN Junyu,BAO Yiyi,JIA Shaojin,JIANG Pingkai,LYU Yongkang,WU Wei,ZHOU Caihui,LUO Chaohua
DOI: https://doi.org/10.11889/j.1000-3436.2017.rrj.35.050303
2017-01-01
Journal of Radiation Research and Radiation Processing
Abstract:Ethylene-octene copolymer (POE) blended with different contents of intumescent flame retardants (ammonium polyphosphate, pentaerythritol, and melamine) was irradiated by electron beams to prepare flame retardant composite materials. The oxygen index, cone calorimeter, and combustion performance were used to characterize the flame retardant properties. The results showed that the tensile strength as well as the oxygen indices of the composites (about 1~2) increased and the elongation at break decreased with increasing absorbed doses. The combustion process of the composites shortened, and the heat and smoke release of the composites were more concentrated. After irradiation crosslinking at 200 kGy, the total heat release decreased from 94.8 MJ/m2 to 79.1 MJ/m2, the total amount of smoke release decreased from 1122.9 m2/m2 to 928.4 m2/m2, the combustion process reduced by about 25%, the CO release rate decreased from 0.0622 kg/kg to 0.0439 kg/kg, and the CO2 producing rate increased from 1.44 kg/kg to 1.51 kg/kg. Moreover, as the absorbed dose increased, the volume resistivity of the material varied slightly.