Comparative investigations of the crystal structure and photoluminescence property of eulytite-type Ba3Eu(PO4)3 and Sr3Eu(PO4)3.
Haipeng Ji,Zhaohui Huang,Zhiguo Xia,Maxim S Molokeev,Xingxing Jiang,Zheshuai Lin,Victor V Atuchin
DOI: https://doi.org/10.1039/c4dt03887h
IF: 4
2015-01-01
Dalton Transactions
Abstract:In this study, the Ba3Eu(PO4)(3) and Sr3Eu(PO4)(3) compounds were synthesized and the crystal structures were determined for the first time by Rietveld refinement using powder X-ray diffraction (XRD) patterns. Ba3Eu( PO4) 3 crystallizes in cubic space group I (4) over bar 3d, with cell parameters of a = 10.47996(9) angstrom, V = 1151.01(3) angstrom(3) and Z = 4; Ba2+ and Eu3+ occupy the same site with partial occupancies of 3/4 and 1/4, respectively. Besides, in this structure, there exists two distorted kinds of the PO4 polyhedra orientation. Sr3Eu(PO4)(3) is isostructural to Ba3Eu(PO4)(3) and has much smaller cell parameters of a = 10.1203(2) angstrom, V = 1036.52(5) angstrom(3). The bandgaps of Ba3Eu(PO4)(3) and Sr3Eu(PO4)(3) are determined to be 4.091 eV and 3.987 eV, respectively, based on the UV-Vis diffuse reflectance spectra. The photoluminescence measurements reveal that, upon 396 nm n-UV light excitation, Ba3Eu(PO4)(3) and Sr3Eu(PO4)(3) exhibit orange-red emission with two main peaks at 596 nm and prevailing 613 nm, corresponding to the D-5(0) -> F-7(1) and D-5(0) -> F-7(2) transitions of Eu3+, respectively. The dynamic disordering in the crystal structures contributes to the broadening of the luminescence spectra. The electronic structure of the phosphates was calculated by the first-principles method. The analysis elucidats that the band structures are mainly governed by the orbits of phosphorus, oxygen and europium, and the sharp peaks of the europium f-orbit occur at the top of the valence bands.