Atomic Dynamics in Zr-Based Glass Forming Alloys Near the Liquidus Temperature
Sri Wahyuni Basuki,Fan Yang,Elisabeth Gill,Klaus Raetzke,Andreas Meyer,Franz Faupel
DOI: https://doi.org/10.1103/physrevb.95.024301
2017-01-01
Abstract:We report simultaneous radiotracer diffusion experiments of Co-57 and of Zr-95 in binary Zr64Ni36, Zr36Ni64, and ternary Zr(60)Ni(25)AL(15) alloys above but near the liquidus temperature (T-l). In contrast to the multicomponent Zr46.75Ti8.25Cu7.5Ni10Be27.5 (Vit4), where a significant component decoupling at the T-l is observed, the ratio between Zr and Co self-diffusion coefficients is smaller than two in the alloys with fewer components. The difference in the degree of decoupling compared to Vit4 can be explained in terms of different T(l)s. Moreover, owing to the high accuracy of the simultaneous tracer diffusion technique, we are able to resolve a small but notable composition dependence of the ratio D-co/D-zr, which decreases with increasing Zr content for all glass forming alloys reported here. In contrast to a hard sphere (HS)-like mixture, where decoupling is controlled only by atomic sizes, this indicates a coupling of the Co/Ni and Zr diffusion, due to the strong chemical affinity between the diffusing components. Our results are in very good agreement with recent simulations in Zr64Ni36 based on mode coupling theory (MCT).