Abstract:Manganese oxides were fabricated by hydrothermal reactions of KMnO4 and MnSO4 solutions. Crystal structures and morphologies of samples were characterized by X-ray diffraction, scanning electron microscopy, Brunauer-Emmett-Teller (BET) measurements, Fourier transform infrared spectroscopy, and thermogravimetric analysis. The combined effects of temperature, additives of H2SO4, and tetrabutylammonium bromide (TBAB) on manganese oxide crystal structures were investigated. The key factors affecting catalytic activity and electrochemical performance of manganese oxides were studied using oxidation of benzyl alcohol and cyclic voltammetry, respectively. The results indicated that pyrolusite (OMS-7) was formed in 0.1 mol.L-1 MnSO4 solution with KMnO4/MnSO4 molar ratios of 7:18 and 8:17 at 120 degrees C, respectively. A mixture of OMS-7 and cryptomelane (OMS-2) was prepared when the molar ratio increased. Potassium ion plays an important role in the formation of OMS-2. Steric effects arose from complexation reactions of TBAB and MnSO4 solutions and facilitated the formation of OMS-2. K-OMS-2 and H-K-OMS-2 were formed by adding 0.1 mol.L-1 TBAB and 0.2 mol.L-1 H2SO4 to 0.1 mol.L-1 MnSO4 solution with a KMnO4/MnSO4 molar ratio of 11:14 at 120 degrees C, respectively. The catalytic oxidation activity was found to follow this trend: H-K-OMS-2 > K-OMS-2 > OMS-7 likely because of the larger amount of acid sites in H-K-OMS-2. However, the exchangeable active oxygen and specific surface area had a greater impact on the electrochemical performance of manganese oxides. The electrocatalytic activity of synthesized manganese oxides for oxygen reduction increased in the order: OMS-7 < H-K-OMS-2 < K-OMS-2. Supercapacitor performance was compared, and the capacitance also increased in the sequence: OMS-7 < H-K-OMS-2 < K-OMS-2.

Porous Magnetic Manganese Oxide Nanostructures: Synthesis and Their Application in Water Treatment.

Ordered Magnetic Core–manganese Oxide Shell Nanostructures and Their Application in Water Treatment

Synthesis Of Porous Magnetic Ferrite Nanowires Containing Mn And Their Application In Water Treatment

Facile Synthesis of Monodisperse Manganese Oxide Nanostructures and Their Application in Water Treatment

Magnetic Fe3O4 Nanoparticles: Synthesis and Application in Water Treatment

Anion-assisted one-pot synthesis of 1D magnetic alpha- and beta-MnO2 nanostructures for recyclable water treatment application

Synthesis and Characterization of Single‐Crystalline MnFe2O4 Ferrite Nanocrystals and Their Possible Application in Water Treatment

Functionalization of carbon nanotubes with magnetic nanoparticles: general nonaqueous synthesis and magnetic properties.

Simultaneous Oxidation and Immobilization of Arsenite from Water by Nanosized Magnetic Mesoporous Iron Manganese Bimetal Oxides (Nanosized-Mmim): Synergistic Effect and Interface Catalysis

One-pot synthesis of hierarchical magnetite nanochain assemblies with complex building units and their application for water treatment

Controlled Preparation of MnO2 Hierarchical Hollow Nanostructures and Their Application in Water Treatment

Controllable Hydrothermal Synthesis of Manganese Dioxide Nanostructures: Shape Evolution, Growth Mechanism and Electrochemical Properties

Hydrothermal Preparation of Nanostructured Manganese Oxides (mnox) and Their Electrochemical and Photocatalytic Properties

Synthesis of MnFe2O4@Mn-Co oxide core-shell nanoparticles and their excellent performance for heavy metal removal.

Endowing Manganese Oxide with Fast Adsorption Ability Through Controlling the Manganese Carbonate Precursor Assembled in Ionic Liquid.

Hydrothermal synthesis of manganese oxide nanomaterials and their catalytic and electrochemical properties

Synthesis of a Thin-Layer MnO2 Nanosheet-Coated Fe3O4 Nanocomposite As a Magnetically Separable Photocatalyst

Assembly Of Maghemite Nanoparticles Into Particulate Nanosheets And Their Application In Wastewater Treatment

Rapid Removal and Separation of Iron(ii) and Manganese(ii) from Micropolluted Water Using Magnetic Graphene Oxide.

Hydrothermal Synthesis And Electrochemical Properties Of Mno2 Nanostructures

One-pot synthesis of nano-MnFe<sub>2</sub>O<sub>4</sub> decorated Al<sub>2</sub>O<sub>3</sub> and its application in Cu<SUP>2+</SUP> adsorption