Dual precipitating reagents-assisted deep blue-emitting borate and near-white oxide-based luminescent materials
Mridula Ghosh,Bibhuti Bhusan Nayak
DOI: https://doi.org/10.1039/d4dt00290c
IF: 4
2024-05-17
Dalton Transactions
Abstract:The work explores dual precipitating reagents-assisted Ce-based deep blue emitting borate and near-white oxide-based luminescent materials. The first precipitating reagent, i.e., aqueous sodium borohydride, was used till the gelation, and the second precipitating reagent, i.e., ammonia solution, was further employed to prepare as-synthesized powders. The XRD, FTIR, and Raman analysis of the calcined powders ranging from 1000 °C – 1400 °C confirmed the development of the primary borate phase, i.e., nearly polyhedral-shaped YBO3 with secondary phases of (Y, Al)BO3 and oxide. However, the preliminary oxide phase, i.e., elongated/rod-like YAG, and secondary phases of YBO3, Al2O3, and CeO2 were developed at 1500 °C with varying holding times. The emission behavior and CIE coordinates confirmed that the borate, i.e., the YBO3-based sample, exhibited a deep blue color. However, the oxide, i.e., the YAG-based sample, showed tunable color emissions from light blue to near white with increased holding time. The average lifetime of the prepared samples varied between 788 ns and 891 ns, which indicates a long decay time. The quantum yield of the sample calcined at 1400-1500 °C varied between ~61 % and ~77 %. Based on the emission behavior, CIE diagram, CCT, powder color, average lifetime, and quantum yield, the developed deep blue emitting borate and light blue/near white oxide-based luminescent materials may be used in the lighting industries.
chemistry, inorganic & nuclear