Abstract:In this study, a series of novel contorted hyberbranched polyimides (HBPIs) were successfully prepared based on commercially available monomers 4,4′-(hexafluoroisopropylidene)diphthalic anhydride (6FDA), 1,1′-binaphthyl- 2,2′-diamine (BNDA), and 1,3,5-tris(4-aminophenyl) benzene (TAPB), and the BNDA comonomer was used to create the contorted moieties in polymer backbone. Experimental results demonstrated that all the prepared HBPIs possessed high glass transition temperatures (Tg = 309~325 °C), excellent thermal stability (Td,5% = 489~503 °C), and their PAA precursors had high number-averaged molecular weights (Mn = 2.9 × 104~5.6 × 104 g/mol). Furthermore, the effect of the degree of contorted moieties in HBPIs changing by the different molar ratios of TAPB:BNDA on polymeric fractional free volumes (FFV) and gas transport properties was systematically investigated. As a result, with the increasing content of BNDA monomer, the gas permeabilities of HBPI membranes were significantly increased. For example, the CO2 and O2 permeabilities of HBPI membrane with the molar ratio of TAPB:BNDA = 4:6 were respectively about 2.8 and 3.2 times higher than that of HBPI membrane without any contorted moieties. Besides, it also maintained reasonable selectivities for CO2/CH4 (~46.3) and O2/N2 (~5.7). These encouraging results were related to the synergetic effects of incorporating contorted sites and improving polymer rigidity by using monomers BNDA and TAPB in copolymerization reaction. Furthermore, no gelation occurred during polymerizations due to the adopted low-temperature synthesis technique that can effectively avoid the high local concentration of the added 6FDA monomer. This work provides a new insight to produce high performance contorted HBPIs containing binaphthyl structures without risk of gelation and also shows a potential application in gas separation.

Gas permeability of fluorinated hyperbranched polyimide

Gas permeation properties of hyperbranched polyimide membranes

Gas transport performance of highly heat-resistant and organo-soluble fluorinated polyimides with bulky pendant group

Preparation and characterization of highly heat-resistant, soluble, and hydrophobic fluorinated polyimides with gas transport properties

High-barrier polyimide containing fluorenol moiety: Gas barrier properties and molecular simulations

Synthesis, characterization, and gas separation properties of novel fluorinated co-polyimides with bulky side groups

Gas Permeation Properties of Hydroxyl-Group Containing Polyimide Membranes

Effect of monomer moieties on the aggregate structure and gas transport properties of polyimides: Insights from experiments and simulations

Low-temperature synthesis and gas transport properties of novel contorted hyperbranched polyimides containing binaphthyl structures

From a hyperbranched polyimide to a microporous network polyimide via reaction temperature change and its application in gas separation membranes

Gas Transport Properties of A Polyimide Based on 2,2-Bis(3,4-decarboxyphenyl) Hexafluoropropane and Meta-Phenylenediamine

Hyperbranched Polyimides for Gas Separation Applications. 1. Synthesis and Characterization

Highly soluble fluorinated polyimides with promising gas transport performance and optical transparency

Fluorinated Biphenyl Aromatic Polyimides for Gas Separation Applications: Real Gas Mixture Study

Acetate-Functional Thermally Rearranged Polyimides Based on 2,2-Bis(3-amino-4-hydroxyphenyl)hexafluoropropane and Various Dianhydrides for Gas Separations

Gas Separation Properties Of Polymers Containing Fluorene Moieties

Fabrication, Facilitating Gas Permeability, and Molecular Simulations of Porous Hypercrosslinked Polymers Embedding 6FDA-Based Polyimide Mixed-Matrix Membranes

Synthesis and properties of fluorinated polyimides from 1,1-bis(4-amino-3,5-dimethylphenyl)-1-(3,4,5-trifluorophenyl)-2,2,2-trifluoroethane and various aromatic dianhydrides

Preparation and Gas Transport Properties of Thermally Induced Rigid Membranes of Copolyimide Containing Cardo Moieties

Synthesis, gas barrier and molecular simulation of intrinsic high-barrier polyimide bearing carbazole and amide

Intrinsically Microporous Polyimides Derived from 2,2′-Dibromo-4,4′,5,5′-bipohenyltetracarboxylic Dianhydride for Gas Separation Membranes