Synthesis, Characterization and Properties of Microporous Lanthanide Silicates: K8Ln3Si12O32NO3·H2O (ln = Eu, Tb, Gd, Sm)
Xi Wang,Jiyang Li,Guangmei Wang,Yide Han,Tan Su,Yi Li,Jihong Yu,Ruren Xu
DOI: https://doi.org/10.1016/j.solidstatesciences.2009.04.005
IF: 3.752
2010-01-01
Solid State Sciences
Abstract:A family of microporous lanthanide silicates, K8Ln3Si12O32NO3·H2O (denoted LnSiO-CJ3, Ln=Eu, Tb, Gd, Sm), was synthesized under mild hydrothermal conditions at 503K. The X-ray powder diffraction patterns of these compounds reveal that they are isostructural. The structure of EuSiO-CJ3 was determined by single-crystal X-ray diffraction analysis. It crystallizes in triclinic space group P-1 (No. 2) with a=11.599(2)Å, b=12.225(2)Å, c=13.829(3)Å, α=112.99(3)°, β=92.05(3)°, γ=90.57(3)°. The structure is based on [Si3O8]n4n− layers with 6-, 8-, 12-rings that are connected by EuO6 octahedra to form a 3-D framework with 8-ring channels along the [001] direction. Charge neutrality is achieved by the K+ and NO3− ions located in the channels. The framework of EuSiO-CJ3 shows good thermal stability, which can be stable up to 1273K. Ion-exchange capacity of EuSiO-CJ3 was investigated by the exchange of NO3− ions with halide ions (F−, Cl−, Br−). The peaks in the emission spectra of LnSiO-CJ3 (Ln=Eu, Tb) belong to the characteristic transitions of Ln3+ (Ln=Eu, Tb) respectively. The lifetime measurements of LnSiO-CJ3 (Ln=Eu, Tb) suggest the presence of three Ln3+ (Ln=Eu, Tb) environments, which are consistent with the crystallographic results.