WANG Hai-feng,XU Yi,PAN Cong-gen,WEI Mei-ying,LUO Zhong-kuan,YANG Hui,WANG Wen-li,WANG Hai-lian
2012-01-01
Abstract:Nanometer Al2O3 filled PTFE composite materials were prepared through mechanical mixing and ultrasonic bathing in ethanol,and the effects of the Al2O3 content,surface modification on the properties of complex materials(such as density,hardness,mechanical and grinding properties) were studied.The results showed: as the content of modified Al2O3 was less than 5%,the tensile strength,the hardness of the resulted materials were higher that of non-modified Al2O3 filled complex materials in the same filler content;as the content of modified Al2O3 was 1% or 9%,the wear mass loss of the resulted materials was 55 or 286 times lower than that of pure PTFE,respectively.However,as the content of non-modified Al2O3 were 1% or 9%,the wear mass loss of the resulted materials were 7 or 420 times lower than that of pure PTFE,respectively.The densities of complex materials kept almost constant,although the change of Al2O3 content and the surface modification with KH560.The friction coefficient of complex materials decreased and then increased with the increase of Al2O3 content,and,as the content of non-modified Al2O3 was 1% and the content of modified Al2O3 was 3%,the resulted materials had the lowest friction coefficient.