Fabrication and Characterization of Er~(3+),Yb~(3+):Y_3Al_5O_(12) Upconversion Luminescent Nanofibers

Dong Xiangting,Gao Xubo,Wang Jinxian,Fan Lijia,Liu Guixia

DOI: https://doi.org/10.3788/AOS20103007.1883

2010-01-01

Acta Optica Sinica

Abstract:In order to obtain upconversion nanofibers materials of a new morphology,PVP/[Y(NO3)3+Al(NO3)3+Er(NO3)3+Yb(NO3)3] composite fibers were prepared by electrospinning,and Er3+,Yb3+∶Y3Al5O12(Er3+,Yb3+∶YAG for short) upconversion nanofibers were fabricated by calcination of the as-prepared composite nanofibers.Thermogravimetry and differential thermal analysis(TG-DTA) revealed that the water,organic compounds and nitrate salts in the composite nanofibers were decomposed and volatilized totally,and the weight of the sample kept constant when temperature was above 550 ℃,and the total weight loss percentage was 90.2 %.X-ray diffraction(XRD) results showed that the composite nanofibers were amorphous in structure,and pure phase Er3+,Yb3+∶YAG nanofibers were obtained by calcination of the relevant composite fibers at 900 ℃ for 10 h.Fourier transform infrared spectrometer(FTIR) analysis manifested that crystalline Er3+,Yb3+∶YAG upconversion nanofibers was formed at 900 ℃.Scanning electron microscope(SEM) analysis indicated that the diameter of Er3+,Yb3+∶YAG upconversion nanofibers was about 75 nm,and the length was greater than 100 μm.Upconversion emission spectra showed under the excitation of a 980 nm continuous-wave diode laser,Er3+,Yb3+∶YAG nanofibres emitted green and red upconversion emissions centered at 522,554 and 650 nm,respectively.The green(522 nm and 554 nm) and red(650 nm) emissions were attributed to the transitions of 2H11/2/4S3/2→4Il5/2 and 4F9/2→4Il5/2 energy levels of Er3+ ions.The formation mechanism of the Er3+,Yb3+∶YAG nanofibers were preliminarily discussed.This method could be applied to prepare the other rare earths garnet-typed compound nanofibers.