Influence of Heat Treatment Temperature on Characteristics of TiO2 Film Photocatalyst

仇雁翎,赵建夫,李田,朱志良

DOI: https://doi.org/10.3321/j.issn:0253-374x.2008.06.011

2008-01-01

Abstract:Development of immobilized TiO2 photocatalyst has become highlight of relevant study in order to facilitate the photocatalytic technology into practical water treatment application.Sol-gel method was used to prepare TiO2 film on fiberglass net.The morphology and structure of the TiO2 film catalysts under different heat treatment temperatures were systematicaly investigated by thermal gravimeter/differential scanning calorimeter(TG/DSC),TiO2 loading measurement,X-ray diffractometer(XRD),scanning electron microscopy(SEM) and so on.The photocatalytic efficiencies of the catalysts made under different heat treatment temperatures were evaluated by the degradation of phenol in solution.Results show that the anatase reaches the highest content and the biggest size for crystalline grain at 500 ℃ out of the adopted four calcination temperature(namely 350,400,450 and 500 ℃).In company with the increasing heat treatment temperature,the monolayer loading amount of TiO2 film gets higher and its photocatalytic degradation ability of phenol in solution was improved.Under the conditions of 2 mg·L-1 of initial phenol concentration and 2 h of reaction time,the phenol removal efficiency are all over 90% for catalysts made with four different calcination temperatures.