Abstract:At the room temperature, a novel and environmental friendly approach for synthesizing polyaniline (PANI) nanofibers on a large scale is presented firstly in the aqueous phase by ultraviolet (UV)-assisted polymerization using cetyltrimethylammonium bromide (CTAB) as the "soft-template." It is obvious that the polymerization process can be accelerated under the illumination of UV light and the preliminary mechanism has been pointed out. Furthermore, it also can be noted that the lower concentrations of CTAB and HCl are helpful for the fabrication of smooth and uniform PANI nanofibers. As observed with FE-SEM and TEM, the as-synthesized PANI nanostructures under the appropriate conditions are composed of uniform nanofibers with the average diameter of about 100 nm and the length of several micrometers. Subsequently, the synthesized PANI nanostructures are characterized with UV-vis, FTIR, XRD spectra, and the typical physical and chemical properties of PANI are displayed. In addition, the conductivity of the synthesized PANI nanofibers was also measured with the four probe method and the excellent conductivity was presented. In summary, the procedure presented here only involving exposure of an acidic aqueous solution of aniline to UV light illumination is so simple and the needed equipment is so low cost, from the viewpoint of technological applications, that the large-scale UV-assisted polymerization of PANI nanofibers from the monomer solution is feasible and promising.

Facile Fabrication of Monolayered Hollow Submicrospheres of PANI on Surfaces of Modified Polymer Films

Fabrication of one dimensional polyaniline nanofibers by UV-assisted polymerization in the aqueous phase.

First Successful Post-Synthetic Self-Assembly of Polyaniline with Poly(N-vinylpyrrolidone) into Aqueous Nanocolloids

Fabrication of shape-controllable polyaniline micro/nanostructures on organic polymer surfaces: obtaining spherical particles, wires, and ribbons.

A Very Thin Layer of NiO, Ni(OH)2 Nanosheets Arrays with Organic Functional Modification of Polyaniline

Synthesis of Highly Hydrophilic Polyaniline Nanowires and Sub‐Micro/Nanostructured Dendrites on Poly(propylene) Film Surfaces

Oxidative Graft Polymerization of Aniline on the Modified Surface of Polypropylene Films

Oxidative graft polymerization of aniline on the surface of poly(propylene)-graft-polyacrylic acid films

A Facile and Efficient Route for Coating Polyaniline Onto Positively Charged Substrate

Fabrication of self-assembled polyaniline films by doping-induced deposition

Controlling the Morphology of Micrometre-Size Polystyrene/polyaniline Composite Particles by Swelling–Diffusion–Interfacial-Polymerization Method

Oxidation−Reduction Reaction Driven Approach for Hydrothermal Synthesis of Polyaniline Hollow Spheres with Controllable Size and Shell Thickness

Controlling the Structure and Morphology of Monodisperse Polystyrene/Polyaniline Composite Particles

Polyacetylene Nanoparticles-Based Preparation of Polyaniline Nanofibers

Superhydrophobic Polyaniline Hollow Bars: Constructed with Nanorod-Arrays Based on Self-Removing Metal-Monomeric Template

Facile Synthesis of Polyaniline‐Polypyrrole Nanofibers for Application in Chemical Deposition of Metal Nanoparticles

Preparation of superparamagnetic polyaniline hybrid hollow microspheres in oil/water emulsion with magnetic nanoparticles as cosurfactant

The Preparation and Characterization of Polyacrylonitrile-Polyaniline (PAN/PANI) Fibers

The Synthesis of Polyaniline in Polyethylene Films with Grafted Sulfonated Polystyrene and Properties of These Films

A facile strategy for synthesis of multilayer and conductive organo-silica/polystyrene/polyaniline composite particles.

Polyaniline Nanotubes Prepared by One-Step Synergistic Polymerization of Aniline and Acrylic Acid